美国ASTMA580-98不锈钢丝标准（中文翻译稿,仅供学习参考）
ASTM A580/580M-98
Standard Specification for Stainless Steel Wire不锈钢丝的标准规范
1. Scope 范围
越狱第三季剧情介绍1.1 This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly ud types of stainless steels for general corrosion resistance and high-temperature rvice. For bars in straightened and cut lengths, e Specifications A276 or A479/A479M.
本规范包括除了自由加工类型以外的不锈钢丝。包括只为较常用的一般耐腐蚀和用于高温类型的（截面为）圆形、方形、八角形、六角形等钢丝型材，仅限线圈。对于在拉直和定尺长度的棒材，见规范A276或A479/A479M。
NOTE 1 ---- For free-machining stainless wire, designed especially for optimum machinability, e Specification A581/A581M.
ditto什么意思注1：对于自由加工的不锈钢丝，尤其为优化可加工性设计的不锈钢丝，见规范A581/A581M。
1.2 The value stated in either inch-pound units or SI(metric) units are to be regarded parately as standards; within the text and tables, the SI units are shown in [brackets]. The values stated in each system are not exact equivalents; therefore, each system must be ud independently of the other. Combining values from the two systems may result in nonconformance with the specification.
无论是英制单位还是公制单位的值均被视作标准；在正文和表格内，公制单位显示在括号[ ]内。每种单位系统的值不是精确相等的；因此每个单位系统应单独使用而不得混用。两个系统的值混合会导致结果不符合规范。
great fire wall1.3 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.
除非订单适用“M”规范，材料供应时须按英制单位。
2. Referenced Documents 引用文件
2.1 ASTM Standards:
A276 Specification for Stainless and Heat-Resisting Steel Bars and Shapes
gre是什么
不锈钢和耐热钢钢棒和型材规范
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
钢铁产品机械性能测试的方法和分析
A479/A479M Specification for Stainless and Heat-Resisting Steel Bars, and Shapes for U in Boilers and Other Pressure V esls
锅炉和其他压力容器用不锈钢和耐热钢钢棒和型材规范
A555/A555M Specification for General Requirements for Stainless Steel Wire and Wire R如何查询考研成绩
ods 不锈钢钢丝和盘条的一般要求规范
A581/A581M Specification for Free-Machining Stainless Steel Wire and Wire Rods
just so you know自由加工的不锈钢钢丝和盘条规范
E527 Practice for Numbering Metals and Alloys (UNS)
金属和合金的编号方式（统一编号系统）
2.2 Society of Automotive Engineers Standard: 汽车工程师协会标准
据有
J1086 Numbering Metal and Alloys
social network金属和合金的编号方式
3. Ordering Information 订货须知
3.1 It is responsibility of the purchar to specify all requirements that are necessary for material ordered under this specification. Such requirements may include, but are not limi耐心的英文
ted to, the following:
买方有责任在按此规范订购材料时指定全部必需的要求。这些要求包括、但不限于以下要求：
3.1.1 Quantity (weight), 质量（重量）
3.1.2 Name of material (stainless steel), 材料名称（不锈钢）
3.1.3 Type or UNS designation (Table 1), 材料类型或UNS（统一编号系统）的名称
3.1.4 Condition (
4.1), 条件
3.1.5 Finish (
4.2), 表面
3.1.6 Cross ction (round, square, etc.), 端面（圆形、方形等）
bellow
3.1.7 Applicable dimensions including size, thickness and width. 适当的尺寸，包括大小、厚度、宽度
3.1.8 ASTM designation A580/A580M and date of issue. ASTM标准名称A580/A580M和发行时间
3.1.9 Coil diameter (inside or outside diameter, or both) and coil weight. 卷的尺寸（内径、外径或两者）和重量
3.1.10 Special requirements. 特殊要求
NOTE 2 ---- A typical ordering description is as follows: 5000lb [2000kg] type 304, wire, annealed and cold drawn, 1/2 in. [13 mm] round, ASTM Specification A580/A580M dated ____. End u: machined hydraulic coupling parts.
注2：典型的订单描述这这样的：5000lb[2000kg]的304钢丝、退火和冷拔、1/2英寸[13 mm]的圆形、规范是ASTM A580/A580M—日期。最终用途：机械加工的水压接头零件。
4. Manufacture 制造
4.1 Condition (Table 2): 状态（表2）
4.1.1 Condition A ---- Annealed as a final heat treatment. Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength.
状态A——退火作为最终的热处理。条件A的材料可以通过冷拔来控制大小尺寸和表面质量，或两者。可稍微提高抗拉强度。
4.1.2 Condition B ---- Cold worked to higher strength.
状态B——冷作提高强度。
4.1.3 Condition T ---- Heat treated to an intermediate temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
状态T——通常把奥氏体在相对低的温度下淬火、回火，热处理到一种中间的回火状态。4.1.4 Condition H ---- Heat treated to a hard temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
状态H——通常把奥氏体在相对低的温度下淬火、回火，热处理到一种硬的回火状态。
4.2 Finish: 表面质量
4.2.1 Cold Drawn ---- A finish resulting from a final cold drawing pass, generally with cold drawing lubricant left on. Special bright finishes, lubricant removal, etc., for special end us must be negotiated with the producer.
冷拔——通过最后冷拔得到的表面，通常残留冷拔润滑剂。特殊的光亮表面、去处润滑剂等特别的最终用途要求需与生产者协商。
4.2.2 Annealed and Pickled --- A dull matte appearance necessarily associated with the dead-soft condition when no final cold drawing is permitted.