DuPont ™ Zytel ®
HTN
high performance polyamide resin
PRELIMINARY DATA
Zytel ®
HTN53G50HSLRHF BK083
Value
DAM
50%RH
Identification Part Marking Code ISO 11469>PA-GF50< Part Marking Code SAE J1344
>PA-GF50<
Mechanical Stress at Break ISO 527MPa (kpsi)
250 (36.2)
网云Strain at Break ISO 527% 2.4 Tensile Modulus ISO 527MPa (kpsi)16800 (2430) Flexural Modulus ISO 178MPa (kpsi)15000 (2170) Flexural Strength
ISO 178
MPa (kpsi)
370 (53.6)
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm. Test temperatures are 23°C unless otherwi stated.
The above data are preliminary and are subject to change as additional data are developed on subquent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2009
090326/090326
The information provided in this data sheet corresponds to our knowledge on the subject at the date of its publication. This information may be subject to revision as new knowledge and experience becomes available. The data provided fall within the normal range of product properties and relate only to the specific material designated; the data may not be valid for such material ud in combination with any other materials, additives or pigments or in any process, unless expressly indicated otherwi The data provided should not be ud to establish specification limits or ud alone as the basis of design; they are not intended to substitute for any testing you may need to conduct to determine for yourlf the suitability of a specific material for your particular purpos. Since DuPont cannot anticipate all variations in actual end-u conditions DuPont makes no warranties and assumes no liability in connection with any u of this information. Nothing in this
publication is to be considered as a licen to operate under or a recommendation to infringe any patent rights. DuPont advis you to ek independent counl for a freedom to practice opinion on
the intended application or end-u of our products. CAUTION: Do not u DuPont materials in medical application involving implantation in the human body or contact with internal body fluids or tissues unless the material has been provided from DuPont under
a written contract that is consistent with DuPont policy regarding medical applications and expressly acknowledges the contemplated u. For further information, plea contact your DuPont reprentative. You may also request a copy of DuPont POLICY Regarding Medical Applications H-50103-3 and DuPont CAUTION Regarding Medical Applications … H-50102-3
Zytel ® HTN53G50HSLRHF BK083 is a 50% glass reinforced, lubricated high performance polyamide resin with improved flow, developed for structural applications requiring excellent surface appearance with water-heated molds.
Property
Test Method
Units
During molding, u proper protective equipment and adequate ventilation. Avoid exposure to fumes
and limit the hold up time and temperature of the resin in the machine. Purge degraded resin carefully with HDPE.
Zytel
®
HTN53G50HSLRHF BK083
Value
DAM
50%RH
Mechanical
Notched Charpy Impact Strength ISO 179/1eA
kJ/m 2
-40°C (-40°F)18 23°C (73°F)
16
Unnotched Charpy Impact Strength ISO 179/1eU
春节放烟花的作文kJ/m
2
-30°C (-22°F)6055
矩形面积
23°C (73°F)95
Thermal
Deflection Temperature ISO 75-1/-2 °C (°F)
1.80MPa
238 (460)
Melting Temperature ISO 11357-1/-3 °C (°F)
惠阳淡水
10°C/min, First Heat 260 (500)
CLTE, Parallel ISO 11359-1/-2
E-4/C (E-4/F)
-40 - 23°C (-40 - 73°F)0.15 (0.08) 23 - 55°C (73 - 130°F)0.10 (0.06) 110 - 200°C (230 - 400°F)0.10 (0.06)
CLTE, Normal ISO 11359-1/-2
E-4/C (E-4/F)
-40 - 23°C (-40 - 73°F)0.55 (0.31) 23 - 55°C (73 - 130°F)0.55 (0.31) 110 - 200°C (230 - 400°F)
1.0 (0.56)
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electri
cal properties measured at 2.0mm, and all ASTM properties measured at 3.2mm. Test temperatures are 23°C unless otherwi stated.
The above data are preliminary and are subject to change as additional data are developed on subquent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2009
090326/090326
The information provided in this data sheet corresponds to our knowledge on the subject at the date of its publication. This information may be subject to revision as new knowledge and experience becomes available. The data provided fall within the normal range of product properties and relate only to the specific material designated; the data may not be valid for such material ud in combination with any other materials, additives or pigments or in any process, unless expressly indicated otherwi The data provided should not be ud to establish specification limits or ud alone as the basis of design; they are not intended to substitute for any testing you may need to conduct to determine for yourlf the suitability of a specific material for your particular purpos. Sin
ce DuPont cannot anticipate all variations in actual end-u conditions DuPont makes no warranties and assumes no liability in connection with any u of this information. Nothing in this
publication is to be considered as a licen to operate under or a recommendation to infringe any patent rights. DuPont advis you to ek independent counl for a freedom to practice opinion on the intended application or end-u of our products. CAUTION: Do not u DuPont materials in medical application involving implantation in the human body or contact with internal body fluids or tissues unless the material has been provided from DuPont under
a written contract that is consistent with DuPont policy regarding medical applications and expressly acknowledges the contemplated u. For further information, plea contact your DuPont reprentative. You may also request a copy of DuPont POLICY Regarding Medical Applications H-50103-3 and DuPont CAUTION Regarding Medical Applications … H-50102-3
Property
Test Method Units
Zytel
®
HTN53G50HSLRHF BK083
Value
DAM 50%RH
Electrical Surface Resistivity IEC 60093ohm >1E15 Volume Resistivity IEC 60093ohm m
>1E13 Dielectric Constant ASTM D 2520 B不失落
1 GHz 4.3 10 GHz 4.4 3 GHz
4.2
Dissipation Factor ASTM D 2520 B E-4
1 GHz 13
简爱每章节概括2 10 GHz 120
3 GHz 117
Flammability
Flammability Classification UL94
0.83mm HB
Other Density
ISO 1183kg/m 3 (g/cm 3)
1600 (1.60)
Water Absorption ISO 62, Similar to
%
Immersion 24h, 2.0mm 0.7
Molding Shrinkage ISO 294-4
%
Normal, 2.0mm 0.3 Parallel, 2.0mm
0.1Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm. Test temperatures are 23°C unless otherwi stated.
The above data are preliminary and are subject to change as additional data are developed on subquent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2009
090326/090326
The information provided in this data sheet corresponds to our knowledge on the subject at the date
of its publication. This information may be subject to revision as new knowledge and experience becomes available. The data provided fall within the normal range of product properties and relate only to the specific material designated; the data may not be valid for such material ud in combination with any other materials, additives or pigments or in any process, unless expressly indicated otherwi The data provided should not be ud to establish specification limits or ud alone as the basis of design; they are not intended to substitute for any testing you may need to conduct to determine for yourlf the suitability of a specific material for your particular purpos. Since DuPont cannot anticipate all variations in actual end-u conditions DuPont makes no warranties and assumes no liability in connection with any u of this information. Nothing in this
publication is to be considered as a licen to operate under or a recommendation to infringe any patent rights. DuPont advis you to ek independent counl for a freedom to practice opinion on the intended application or end-u of our products. CAUTION: Do not u DuPont materials in medical application involving implantation in the human body or contact with internal body fluids or tissues unless the material has been provided from DuPont under
a written contract that is consistent with DuPont policy regarding medical applications and expressly acknowledges the contemplated u. For further information, plea contact your DuPont reprenta
tive. You may also request a copy of DuPont POLICY Regarding Medical Applications H-50103-3 and DuPont CAUTION Regarding Medical Applications … H-50102-3
Property
Test Method Units
Zytel
®
HTN53G50HSLRHF BK083
Value
DAM 50%RH
Processing
中央空调风管火龙果吃法Melt Temperature Range °C (°F)280-300 (535-570)
Melt Temperature Optimum °C (°F)290 (555) Mold Temperature Range °C (°F)85-105 (190-220)
Mold Temperature Optimum °C (°F)95 (200) Drying Time, Dehumidified Dryer h 6-8 Drying Temperature
°C (°F)100 (210) Processing Moisture Content
%
<0.10
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm. Test temperatures are 23°C unless otherwi stated.
The above data are preliminary and are subject to change as additional data are developed on subquent lots.
The DuPont Oval Logo, DuPont™, The miracles of science™ and Zytel® are trademarks or registered trademarks of DuPont Company. Copyright© 2009
090326/090326
The information provided in this data sheet corresponds to our knowledge on the subject at the date of its publication. This information may be subject to revision as new knowledge and experience becomes available. The data provided fall within the normal range of product properties and relate only to the specific material designated; the data may not be valid for such material ud in combination with any other materials, additives or pigments or in any process, unless expressly indicated otherwi The data provided should not be ud to establish specification limits or ud alone as the basis of design; they are not intended to substitute for any testing you may need to conduct to determine for yourlf the suitability of a specific material for your particular purpos. Since DuPont cannot anticipate all variations in actual end-u conditions DuPont makes no warranties and assumes no liability in connection with any u of this information. Nothing in this
publication is to be considered as a licen to operate under or a recommendation to infringe any patent rights. DuPont advis you to ek independent counl for a freedom to practice opinion on the intended application or end-u of our products. CAUTION: Do not u DuPont materials in medical application involving implantation in the human body or contact with internal body fluids or tissues unless the material has been provided from DuPont under
a written contract that is consistent with DuPont policy regarding medical applications and expressly acknowledges the contemplated u. For further information, plea contact your DuPont reprentative. You may also request a copy of DuPont POLICY Regarding Medical Applications H-50103-3 and DuPont CAUTION Regarding Medical Applications … H-50102-3
Property
Test Method Units