中、美常用铝合金牌号对照及比重

Designation and Specific Gravity of Common

Aluminium Alloy in China and in the United States.

中国 CHINA	美国 THE UNITED STATES	比重 GRAVITY
L3	1050	2.705
L2	1060	2.705
L1	1070	2.70
L5	1200	2.70
L5-1	1100	2.71
L4	1235	2.705
LB1	7072	2.72
LB2	1350	2.705
从头在来LF2	5154	2.66
LF3	5154	2.66
LF4	5083	2.66
LF5-1	5056	2.66
LF5	5456	2.66
LD10	2014	2.80
LY11	2017	2.79
LY1	2217	2.79
LD9	2018	2.82
LD7	2018	2.82
LY12	2024	2.78

LF21	3003	2.73
LD11	4032	2.68
LT1	4043	2.69
LT13	4343	民事起诉状2.68
LT17	4047	2.66
LF43	5457	2.69
LD2	6151	2.71
LD30	6061	2.70
LD31	6063	2.70
LB1	7072	2.72
LC3	7174	2.81
LC9	7075	2.81
LC10	7079	2.88

铝及铝合金状态代号 Temper designations of aluminium and its alloys

国内铝及铝合金状态代号 National temper designations of aluminium and its alloys

单位性质一般怎么填

代号 Code	供应状态 Temper as supplied	代号 Code	供应状态 Temper as supplied	代号 Code	供应状态 Temper as supplied
Y	冷作硬化 Cold work hardened	CZ	淬火自然时效 Quenched. naturally aged	CSO	淬火人工时效优质表面 Quenched.Artificially..aged high-quality surface
Y2	半冷作硬化 Half work hardened	CZO	淬火自然时效、优质表面 Quenched. naturally aged.high-quality surface	CSY	淬火人工时效冷作硬化 Quenched.artificially aged cold work hardened
M	退火 Annealed如何组建局域网	CZY	淬火自然时效、冷作硬化百度文库 - 让每个人平等地提升自我Quenched. ld work hardened	CgS2	淬火变级人工失效状态 Quenched.two step artificially aged
O	优质表面 high-quality surface	CZYO	淬火自然时效、冷作硬化、优质表面 Quenched. ld work hardened high-quality surface	R	热加工 Hot worked
MO	退火、涂漆优质表面	代号 Code	无愧是什么意思冷变形后稳定化处理 Stabilized after cold forming	J	加厚包铝 Thickening clad
B	不包铝 Unciad	CZ	不包铝淬火自然时效冷作硬化 Unciad. Quenched. Naturally aged. Cold work hardened	Y1	雪的简笔画 3/4硬 3/4 hard
BM	不包铝、退火 Unciad. annealed	CZO	淬火人工时效 Quenched.artificialy aged	Y4	1/4硬 1/4hard
Q	涂漆优质表面 Painted.High-quality surface	CZY	矛拉伸 Pre-stretched

常用国际标准状态代号ISO temper designations

代号 Code	调质说明Description	代号 Code	调质说明Description
F O H H12 H14 H16 H18 H19 H22 H24 H26 H112 H116	加工状态 As fabricated 退火状态 Annealed 加工硬化 Work hardened 通过加工硬化获得相当于1/4硬状态的性能 Applies to products which are work hardened to provide property equivelant to 1/4 hard 通过加工硬化获得相当于1/2硬状态的性能 Applies to products which are work hardened to provide property equivelant to 1/2 hard 通过加工硬化获得相当于3/4硬状态的性能 Applies to products which are work hardened to provide full hardened property 通过加工硬化获得全硬状态的性能 Applies to products which are work hardened to provide full hardened property 家鹅通过加工硬化获得超硬状态的性能 Applies to products which are work hardened to provide extra hardened property 加工硬化后进行不完全退火获得相当于1/4硬状态的性能 Applies to products which are partially annealed after work hardening to provide property equivelant to 1/4 hard 加工硬化后进行不完全退火获得相当于1/2硬状态的性能 Applies to products which are partially annealed after work hardening to provide property equivelant to 1/2 hard 加工硬化后进行不完全退火获得相当于3/4硬状态的性能 Applies to products which are partially annealed after work hardening to provide property equivelant to 3/4 hard 高温下加工获得的状态，有性能要求 Temper available from high temperature operation. There is requirement for peoperty Al、Mg系合金的一种专门加工硬化的状态，材料有高的抗应力腐蚀性能 Special work hardened temper for Al-Mg ries. The materials are kf high stress corrosion resistance	H32 H34 H36 H321 T3 T4 T6 步骤图T62 T651 T8 T851	加工硬化后再经稳定化处理获得当相于1/4硬状态的性能 Applies to products which are stabilized after work hardening to provide equivelant to 1/4 hard 加工硬化后再经稳定化处理获得相当于1/2硬状态的性能 Apples to products which are stabilized after work hardening to provide property equivelant to 1/2 hard 加工硬化后再经稳定化处理获得当相于3/4硬状的性能 Applies to products which are stabilized after work hardening to provide property equivelant to 3/4 hard 热加工及冷加工的加工硬化程度都比H32稍小的状态。 Temper who work hardening extent kf hot and working is less than that of H32 固溶处理，冷加工再经自然时效的状态。 Applies to products which are solution treated ,cold worked and then naturally aged 固溶处理后自然时效的状态 Applies to peoducts which are solution treated ,cold worked and then naturally aged 固溶处理后人工时效的状态 Applies to products which are naturally aged after solution heat treatment 由O或F状态，进行固溶处理后，再进行人工时效状态，也可适用于用户对任何状态的产品进行热处理后的状态 Applies to products which are artificially ,aged from annealed or fabricated condition,also applies to products which are heat treated by buyers 固溶热处理后经拉伸消除应力再进行人工时效 Applies to products which are stress relieved by stretching after solution geat treatment and then artificially aged 固溶热处理，冷加工后再经人工时效的状态 Applies to products which are solution heat treated artificially aged after cold working 固溶热处理，经拉伸消除应力后，再进行人工时效 Applies to products which are solution heat treated artificially aged after stress relieved by stretching