preface前言
this standard was prepared by the Australian members of the joint standards Australia/standards new Zealand committee MT-001 , iron and steel to superde AS2027-1985, iron casting-abrasion-resistant white iron . after consultation with stakeholders in both countries , standards Australia and standards new Zealand decided to develop this standard as an Australian, rather than an Australian/new Zealand standard.
此标准由澳大利亚-新西兰铸铁铸钢标准联合会MT-001成员之一澳大利亚修订，代替AS2027-1985耐磨白口铸铁标准。在协商之后，两个国家都保管这个标准，同时使用这一标准。
The objective of this standard is to specify white cast iron that will not be susceptible to abrasive attack due to its wear resistant properties .
此标准的目的是指定耐磨铸铁的特性。
The revision of AS2027-1977 was initiated by rearch work carried out by a joined panel of csito and mtia , which found that the morphology of complex eutectic carbides in the white cast irons was incorrectly described in that edition. The following editions AS2037-1985 and this edition continue to reflect the results of that rearch.
AS2027-1977 这个版本起初被CSITO和MTIA指定和运行. 此版本中指出的石墨共晶的形态的描述是不正确的，此后的版本AS2037-1985继续了这一错误结果。
The committee decided to change this standard to a materials standard, with the casting aspects being placed in AS4783.
委员会决定改变这个标准成为材料标准，在AS4783中有铸造方面的内容。
This standard is one of a ries of standards covering the range of cast irons, the ries compris the following:这个标准覆盖了铸铁范围内的一系列标准，包含如下：
AS
1830 grey cast iron 灰铸铁
1831 ductile cast iron 球墨铸铁
1832 malleable cast iron 可锻铸铁
1833 austenitic cast iron 奥氏体铸铁
2027 wear-resistant white cast iron(this standard)耐磨白口铸铁
4738 metal castings – ferrous sand moulded 金属型铸造-铁砂型
5049 cast iron – designation of microstructure of graphite 铸铁 石墨的微观组织
There are no international standards (iso) on wear-resistant white iron 在耐磨白口铸铁方面没有国际性的标准
The term ‘informative’ has been ud in this standard to define the application of the appendix to which it applies .An ‘informative’ appendix is only for information and guidance “informative” 在标准中被使用，定义用途。它只是一个信息的说明和指导。
天津枫叶国际学校
1范围
2 参考文件
3 定义
4 名称
5 化学成分
6 金相检查
7 硬度
8 测试结果
9 单独测试
附录
Ａ 耐磨白口铸铁的热处理和金相组织
Ｂ 镍铬类铸铁的在晶粒尺寸和化学成分之间的关系
1 scope范围
This standard specifies requirements for the following types of wear-resistant white cast iron: 本标准规定了下面几类耐磨白口铸铁的要求。
a) White cast iron specified by hardness. 白口铸铁硬度规定
什么口红好
b) Nickel-chromium type.镍铬类
c) High chromium type.高铬类
2 referenced documents 参考文件
The following documents are referred to in this standard: 下面的文件为此标准中的参考文件
AS
1816 metallic materials-brinell hardness test 金属材料布尔硬度测试
1816.1 part1: test method (ISO 6506-1:1999,MOD) 测试方法
2706 numerical values-rounding and interpretation of limiting values 数值计算和限制值的解释
4738 metal casting-ferrous sand moulded 金属型铸造 铁砂模
AS/NZS
1050 methods for the analysis of iron and steel 铸铁和铸钢的分析方法
1050.1 part 1:sampling iron and steel for chemical analysis 铸铁和铸钢化学分析抽样
3 definitions 定义
For the purpo of this standard , the definitions below apply. 本标准的目的，下面要求的定义
山简笔画图片大全
3.1 cast irons 铸铁
Ferrous alloys which contain over two percent carbon, may contain other elements and have a wide range of metallurgical and mechanical properties. 铁合金包含两个百分比的碳，也可以包含其他的合金元素，有较宽的冶金范围和机械性能。
3.2 white iron 白口铸铁
Cast iron that contains generally no graphite, although under certain circumstances a small amount of graphite may be accepted or unavoidable. The chemical composition and heat treatment of the alloy will determine the type of metallic carbides prent in the microstructure 无石墨铸铁总是在某种情况下有较少量的石墨可以被接受或者不可避免，合金的化学成分和热处理将决定了金属碳化物目前的组织。公孙子都
４ 符号标识
吉他初学者
4．1 总则
命名应该包括澳大利亚标准号，ｉ.e.AS2027,后面是/，再后是合适的编号，见条款4.2,4.3,4.4。
4．2 显示硬度的白口铸铁编号。
编码规定：（a）前缀字母“U”表示普通的非合金白口铸铁，后面跟随一个硬度说明
(b)三个数字表示最小的布尔硬度要求。
编号的例子：AS 2027/U350。
4.3 镍铬类
帅气的网名
编号规定
（a）“NiCr”表示主要的合金成分。
（b）一个数字（1,2或者4）表示不同的合金含量 级别
（c）三个数字表示最小的布尔硬度要求
4.4 高铬类
前面主要成分的化学符号，后面是化学成分的含量，中间用空格隔开。
六十四卦图
例如：ＡＳ２０２７/CrMo 15 3
这表示 含Cr合金27%，补充 HC 或 LC,表示不同的含碳量。
5 化学成分
5.1 概述
NiCr类和高Cr类化学成分应该符合表1和2中给出的范围
5.2 取样分析
取样方法按AS/NZS1050.1 化学成分的测定按标准精确执行。
6 金相检测
组织的检测可以在订单接受时商定，如果这样的检测被确定，检测将被执行，检测样取自铸件本体或者附铸或单铸测试块，提供的样块将是和铸件相同的凝固速度凝固的。
欧共体
在询价和下订单的时候，在哪儿检测、取试样的位置和检测的方式及可接受组织标准，也是应该达成一直。注：指导金相组织的说明详见附录A中的A1.2，A2.2和3.2
附录A
A1 白口铸铁关于硬度的说明
A1.1 热处理
这些等级一般在毛坯铸态被提供，热处理要求是为了提高机械性能，这应该在接受订单的时候提出来。
A1.2 组织
组织可以被认为是由渗碳体和珠光体的组成，通常是游离态石墨， 除非在厚大件或缓慢冷却的情况下这种组织是不可避免的，或者被客户所允许。
A2 镍铬类
热处理
对于这类材质，热处理的方式通常是较合理的处理方式。如果在毛坯状态就要求了，这应该在询价或下订单的时候就说明了。推荐的热处理为 HT1，HT2和HT3和下面的说明。HT2和HT3 包括可选择二次阶段的热处理，在第一阶段得到回火马氏体，这能使具有最大的耐冲击力，在询价和订单的时候，客户应该与生产厂商量热处理的类型。
被建议的热处理是可实施的，如下：
HT1 热处理温度在250-300 保温4-16小时后空冷或炉冷
HT2 热处理温度在425-475 保温4-16小时后空冷或炉冷
可选择回火温度在250-300 保温4-16小时后空冷或者炉冷来提高硬度
一般，HT1 被使用在ＡＳ２０２７/Ni Cr1-550 ， HT2 使用在AS2027/Ni Cr2-500, 但是两者也能同时被使用，
AS2027/Ni Cr4-500，AS2027/Ni Cr 4-600 , AS2027/NiCr4-630