Item 序号 | Test Description 测试描述 | Qty on Test (pcs)测试数量 | Conformance 符合 | Non-conformance不符合 | Conformance Rate符合率 | ||||
100 Oven Test（加热测试） | Put the sample into the oven and heat it to 230℃. Then immediately place it into 20℃ water. No crack allowed. 将样品放入烤箱(炉)中加热至230℃，然后立即放入20℃的水中，不允许有破裂。 | 125 | 125 | 0 | 100% | ||||
101 Impact Test碰撞测试 | Drop the steel ball having a weight of 535g from 514mm high onto the glass surface at different points for altogether 3 impacts. No crack and damage allowed. Remark: The impact to the glass edge is not allowed. 将重535克的钢球从离钢化玻璃表面514MM高的地方进行碰撞，要求对不同的点进行三次碰撞，不允许有破裂或损坏。 注：不允许对钢化玻璃边缘进行测试。 | 125 | 125 | 0 | 100% | ||||
102 Density Test 密度测试 | Stick the adhesive tape on the surface of the glass. Crack the glass using a tool having a sharp head. The cracked particles sticked on the tape within the area of 50mm x50mm should be not less than 50 ones but not over 300 ones. 将封箱胶粘贴在玻璃的表面，用带尖头的工具打碎玻璃，粘在面积为50X50MM胶带上的玻璃碎片应不少于50个不大于300个。 Remark: The result is that there are 153 particles by average per square. 注：结果是每平方米153个碎片。 | 125 | 125 | 0 | 100% | 美丽人体||||
Dimension Measurement 尺寸测量 | Critical eagles致命 | 下基层Major 重要缺陷 | Minor 轻微缺陷 | ||||||
200 | Flatness tolerance at the straight surface +0 –1mm. 直平面承受力为+0 –1mm. | 0 | 0 | 0 | |||||
201 | Flatness tolerance at the arc surface +0 –2mm. 弧形面承受力为+0 –2mm. | 0 | 0 | 0 | |||||
202 | Thickness Tolerance +/-0.2mm关于含羞草的资料 厚度承受力为+/-0.2mm | 0 | 0 | 0 | |||||
203 | No wobble allowed( not exceed 1.5mm) 左右摇摆不超过1.5MM | 0忝为 | 0 | 2 | |||||
Appearance Check 外观检测 | |||||||||
300 | Crack on the edge must not exceed 1mm. 玻璃边缘破裂不超过1MM. | 0 | 0 | 0 | |||||
301 | No sharp edges and points on the four corners. 四个角上没有锋利的边或点. | 0 | 0 | 1 | |||||
eosr302 | No dirt and dent on the surface. 表面没有污点 | 0 | 0 | 4 | |||||
303 | Slight scratch (20mm) on the edge must not exceed two ones.玻璃边缘轻微的刮擦（20MM）不能超过2个。 | 0 | 0 | 0 | |||||
Total | 0 | 0 | 7 | ||||||