间距为25 mm时，复合材料易发生界面滑脱和端头断裂失效。
3 结论
（1）帘线/橡胶复合材料在不同帘线层接头搭接形式下的力学行为具有较大非线性，搭接段间距为5 mm时的凹型凸型搭接试样的综合力学性能最优。
（2）帘线/橡胶复合材料的帘线层接头搭接段间距为5和15 mm时，试样失效形式主要为搭接处断裂，此处的帘线层和橡胶层所受应力最大；当搭接段间距为25 mm时，复合材料易发生界面滑脱和端头断裂失效。
参考文献：
[1]张福范.叠层复合材料搭接接头的层间应力[J].中国科学：数学物
绝字开头的成语理学天文学技术科学，1987，17（7）：41-49.
[2]张阿盈.复合材料胶接搭接接头应力分析方法研究[J].航空工程
美女表姐恋上我
进展，2012，3（2）：11-17.
[3]W hitney J.Stress Analysis of a Composite Double-lap Joint Using
Higher Order Plate Theory[C].Kissimmee：Structures，Structural Dynamics & Materials Conference，2013.我与大黑狗
[4]L eslie W，Nabil C，John W，et al.Fatigue Damage Monitoring of a
Composite Step Lap Joint Using Distributed Optical Fibre Sensors[J].
Materials，2016，9（5）：374.
[5]李澄.拼接与搭接铺层对复合材料性能影响研究[J].山东工业技
术，2019（12）：14-15.
[6]陶永强，矫桂琼，王波，等.搭接长度对Z-pins增强陶瓷基复合材料
哪座房子最漂亮接头连接性能的影响[J].材料科学与工程学报，2008，22（4）：593-598.
[7]张丰发，杜星文，匡震邦.拉伸条件下帘线/橡胶复合材料的失效准原创文章
则[J].上海交通大学学报，2005，39（5）：832-835.
[8]郭霞，关志东，刘遂，等.搭接长度对复合材料单搭接胶接接头的影
响[J].科技导报，2013，31（7）：37-41.
[9]陈想，陈波宇.频率和温度对帘线与胶料动态粘合性能的影响[J].
轮胎工业，2020，40（6）：360-362.史上最大地震
[10]李利，刘潇冬，王瑞.试样因素对橡胶-钢丝帘线粘合性能测试的
影响[J].橡胶工业，2018，65（2）：227-230.
收稿日期：2020-11-14
Mechanical Property and Failure Modes of Cord/Rubber Composite
Multilayer Structure
WU Jian，LUO Hang，GUO Xiaonong，ZHAO Yuehao，SU Benlong，LI Zhe，WANG Youshan
wrap
（Center for Rubber Composite Materials and Structures，Harbin Institute of Technology at Weihai，Weihai 264209，China）Abstract：The mechanical property and failure modes of cord/rubber composites with different overlap forms and different distance of overlap ction were studied.The results showed that，the mechanical behavior of cord/rubber composite under different overlap forms was nonlinear，and the comprehensive mechanical properties of the concave-convex overlap form were the best when the distance of the overlap ction was 5 mm.When the distance of overlap ction of cord/rubber composite material was 5 and 15 mm，the main failure mode of samples were the fracture at the overlap joint，where the stress of the cord layer and rubber layer was the largest.When the distance of the overlap ction was 25 mm，the interface slippage and end fracture failure would easily occur.
Key words：cord；rubber；composite；overlap form；distance of overlap ction；mechanical property；failure mode
民间艺术剪纸一种全钢巨型工程子午线轮胎胎面胶
配方及制备方法
由福建省海安橡胶有限公司申请的专利（公布号 CN 111748132A，公布日期 2020-10-09）“一种
全钢巨型工程子午线轮胎胎面胶配方及制备方法”，涉及的全钢巨型工程机械子午线轮胎胎面胶配方为天然橡胶 55～65，炭黑 20～25，白炭黑 5～10，硅烷偶联剂 1～2，氧化锌 2～3，硬脂酸 1～2，防老剂 2～3，软化剂 1～2，防焦剂 0.2～0.5，硫黄 1～2，促进剂 0.5～1；采用两段母炼和一道终炼的方法完成胎面胶制备。
本发明胎面胶适合在煤矿等特定环境中使用。
（本刊编辑部 马 晓）