3
Scotch-W eld TM
Epoxy Adhesives
DP460 Off-White• DP460 NS
Product Description3M™Scotch-Weld™Epoxy Adhesives DP460 Off-White and DP460 NS are high
performance, two-part epoxy adhesives offering outstanding shear and peel
adhesion, and very high levels of durability.
Features• High shear strength• Controlled flow
• High peel strength• 60 minute worklife
• Outstanding environmental performance• Non sag (Scotch-Weld DP460 NS)
• Easy mixing
Typical Uncured Physical Properties Note:The following technical information and data should be considered reprentative or typical only and should not be ud for specification purpos.
Scotch-Weld Scotch-Weld
Epoxy Adhesive Epoxy Adhesive Product DP460 Off-White DP460 NS
Viscosity (approx.)Ba20,000-50,000 cps150,000-275,000 cps @ 73°F (23°C)Accelerator8,000-14,000 cps8,000-14,000 cps
Ba Resin Ba epoxy epoxy
Accelerator amine amine
Color Ba white white
Accelerator amber amber
Net Weight Ba9.3-9.79.3-9.7
Lbs./Gallon Accelerator8.8-9.28.8-9.2
Mix Ratio (B:A)Volume2:12:1
Weight2:0.962:0.96
Worklife, 73°F (23°C)20 g mixed60 minutes60 minutes
10 g mixed75 minutes60 minutes
5 g mixed90 minutes60 minutes
- 1 -
Scotch-W eld
TM
Epoxy Adhesives
DP460 Off-White • DP460 NS
- 2 -
Product
3M™Scotch-Weld™3M™Scotch-Weld™Epoxy Adhesive Epoxy Adhesive DP460 Off-White DP460 NS
Physical Color
Opaque, off-white
Off-white Shore D Hardness 75-80
78-84Thermal
Coefficient of Thermal Below Tg 59 x 10-674.44 x 10-6Expansion Above Tg
159 x 10-6166 x 10-6
(in./in./°C)
Thermal Conductivity
0.104
0.104
动画美女图片(btu - ft./ft.2- hr. - °F) @ 45°C Electrical
Dielectric Strength (ASTM D 149)1100 volts/mil 727 volts/mil Volume Resistivity (ASTM D 257)
2.4 x 1014ohm-cm
3.25 x 1015ohm-cm
Typical Cured
Thermal Properties
Note:The following technical information and data should be considered reprentative
or typical only and should not be ud for specification purpos.
葱花鸡蛋饼的做法Typical Curing Characteristics
中华民间小故事Note:The following technical information and data should be considered reprentative
长大做个好爷爷or typical only and should not be ud for specification purpos.
Rate of Strength Build-Up
电饭煲做蛋糕教程Aluminum, Overlap Shear (7 mil Bondline) (ASTM D 1002-72)Bonds Tested at 73°F (23°C)
Scotch-Weld Epoxy Adhesive DP460 Off-White
Time in Oven
Cure Temperature 73°F (23°C)
120°F 1(49°C)140°F 1(60°C)30 min.—<503000/60260—13004500/602
90—4300/602—2 hr.—4400/60248003—4800/602
—5400——61000——73500—
—
24
4000/602
Scotch-Weld Epoxy Adhesive DP460 NS
1
This reprents the oven temperature to which the bonds were subjected for the prescribed time. The average bondline temperature during the cure time will be somewhat lower than the oven temperature.2
The value in the denominator is the expected minimum 73°F (23°C) T -peel strength (piw) measured after the indicated cure cycle.
NOTE:The data in this T echnical Data Sheet were generated using the 3M™EPX™Applicator System equipped with
an EPX static mixer, according to manufacturer’s directions. Thorough hand-mixing will afford comparable results.
Time in Oven
Cure Temperature 73°F (23°C)
120°F 1(49°C)
160°F 1(71°C)
15 min.—–486030—10525060—280053002 hr.1505054704465400532069705570514024
4500
–
5210
Scotch-W eld
TM
Epoxy Adhesives
DP460 Off-White • DP460 NS
-
3 -
Typical Adhesive Performance Characteristics
Note:The following technical information and data should be considered reprentative or
typical only and should not be ud for specification purpos.
Substrates and Testing
A.Overlap Shear (ASTM D 1002-72)
Overlap shear (OLS) strengths were measured on 1 in. wide 1/2 in. overlap specimens. The bonds were made individually using 1 in. x 4 in. pieces of substrate except for aluminum. Two panels 0.063 in. thick, 4 in. x 7 in. of 2024T-3 clad aluminum were bonded and cut into 1 in.wide samples after 24 hours. The thickness of the bondline was 0.005-0.008 in. All strengths were measured at 73°F (23°C) except where noted.
The paration rate of the testing jaws was 0.1 in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.;other metals, 0.05-0.064 in.; rubbers, 0.125 in.; plastics, 0.125 in.B.T-peel (ASTM D 1876-61T)
T-peel strengths were measured on 1 in. wide bonds at 73°F (23°C). The testing jaw paration rate was 20 inches per minute. The substrates were 0.032 in. thick.C.Bell Peel (ASTM D 3167)
Bell peel strengths were measured on 1/2 in. wide bonds at the temperatures noted. The testing jaw paration rate was 6 in. per minute. The bonds are made with 0.064 in. bonded to 0.025 in.thick adherends.D.Cure Cycle
With the exception of Rate of Strength Build-Up Tests, all bonds, were cured 7 days at 73°F (23°C) at 50% RH before testing or subjected to further conditioning or environmental aging.Aluminum, Overlap Shear, at Temperature (PSI)
3M™Scotch-Weld™3M™Scotch-Weld™Epoxy Adhesive Epoxy Adhesive DP460 Off-White
DP460 NS
-67°F (-55°C)4500490073°F (23°C)
45004650180°F (82°C) (15 min.)17001360(30 min.)110001810(60 min.)114002630(4 hr.)1
25002680250°F (121°C) (15 min.)1
220
420
1Reprents time in test chamber oven before test.
Metals, Overlap Shear, Tested @ 73°F (23°C) (PSI)
Scotch-Weld Scotch-Weld Epoxy Adhesive Epoxy Adhesive DP460 Off-White
教学设计的作用DP460 NS
Aluminum
Etched
45004500Oakite degrea 32002300MEK/abrade/MEK
35002670Cold Rolled Steel Oakite degrea
3500—MEK/abrade/MEK 28003600Copper-MEK/abrade/MEK 40004400Brass-MEK/abrade/MEK —3400CDA 2604000—Cartridge 4200—Stainless Steel
MEK/abrade/MEK
40002400Galvanized Steel-Oakite degrea
Hot dipped
20002480Electrodeposited
2100
3000
Scotch-W eld
TM
Epoxy Adhesives
DP460 Off-White • DP460 NS
- 4 -
Typical Adhesive Performance Characteristics (continued)
Note:The following technical information and data should be considered reprentative
or typical only and should not be ud for specification purpos.
Substrates and Testing (continued)
Aluminum, T-Peel (PIW), at Temperature Aluminum - etched (17-20 mil bondline)
3M™Scotch-Weld™3M™Scotch-Weld™Epoxy Adhesive Epoxy Adhesive DP460 Off-White DP460 NS
-67°F (-55°C)
5-103-573°F (23°C)6060180°F (82°C)
3-5
20
Metals, T-Peel, Tested @ 73°F (23°C) (PIW)
Scotch-Weld Scotch-Weld Epoxy Adhesive Epoxy Adhesive DP460 Off-White
DP460 NS
Aluminum, etched 17-20 mil bondline 60not tested 5-8 mil bondline 50Cold Rolled Steel
17-20 mil bondline Oakite degread 40not tested
MEK/abrade/MEK
25
Other Substrates, Overlap Shear Tested @ 73°F (23°C)
Surf. Prep. 1
Surf. Prep. 2
Scotch-Weld Scotch-Weld Scotch-Weld Scotch-Weld Epoxy Adhesive Epoxy Adhesive Epoxy Adhesive Epoxy Adhesive Substrate
DP460 Off-White DP460 NS
DP460 Off-White DP460 NS
ABS 300
345575
572PVC
50081533503133Polycarbonate 400380500390Polyacrylic 220210330270Polystryene 4503204753490FRP 8005701000313793Phenolic 14003121031400312313SBR/Steel
150313014032393Neoprene/Steel
100
90
1203
1143
1Isopropyl Alcohol Wipe. See Surface Preparation Section D for additional information.2Isopropyl Alcohol/Abrade/Isopropyl Alcohol: See Surface Preparation Section E for
additional information.
3Substrate failure.
Aluminum Bell Peel (PIW), at Temperature (ASTM D 3167)
Scotch-Weld Epoxy Adhesive DP460 NS
-67°F (-55°C)1973°F (23°C)77180°F (82°C)
39
Scotch-W eld
TM
Epoxy Adhesives
DP460 Off-White • DP460 NS
- 5 -
Typical Adhesive Performance Characteristics (continued)
Note:The following technical information and data should be considered reprentative
梦见狗咬人
or typical only and should not be ud for specification purpos.
Substrates and Testing (continued)Environmental Resistance Aluminum (Etched)
Measured by Overlap Shear Tested @ 73°F (23°C) (PSI)1(ASTM D 1002-72)
3M™Scotch-Weld™3M™Scotch-Weld™Epoxy Adhesive Epoxy Adhesive Environment Condition DP-460 Off-White DP-460 NS
73°F (23°C)/50% RH 30 d 252005460Distilled Water 30 d, i 3
51004550Water Vapor
120°F (49°C)/100% RH, 30 d 4500
3920200°F (93°C)/100% RH, 14 d 31003370Antifreeze/H 2O (50/50)180°F (82°C), 30 d, i 50004400Isopropyl Alcohol 73°F (23°C), 30 d, i 57005320Methyl Ethyl Ketone 73°F (23°C), 30 d, i 42004000Salt Spray (5%)95°F (35°C), 30 d 51005200Skydrol LD-4
150°F (66°C), 30 d, i
3700
5250
1Data reported are actual values from the lots tested and may be higher than values published计算机由什么组成
elwhere in this T echnical Data Sheet.
2d = days 3i = immersion
Environmental Resistance Galvanized Steels 1
Measured by Overlap Shear Tested @ 73°F (23°C) (PSI)2(ASTM D 1002-72)
Hot Dipped
Electrodeposited
Scotch-Weld Scotch-Weld Scotch-Weld Scotch-Weld Epoxy Epoxy Epoxy Epoxy Adhesive Adhesive Adhesive Adhesive DP460DP460DP460DP460Environment Condition Off-White NS Off-White NS
73°F (23°C)/50% RH 30 d 32200not tested 2300not tested Distilled Water 30 d, i 4
2300not tested 2300not tested Water Vapor
120°F (49°C)/100% RH, 30 d
1900not tested 2000not tested 200°F (93°C)/100% RH, 14 d
15001000Antifreeze/H 2O (50/50)180°F (82°C), 30 d, i 2000not tested 1950not tested Isopropyl Alcohol 73°F (23°C), 30 d, i 2000not tested 2200not tested Methyl Ethyl Ketone 73°F (23°C), 30 d, i 2000not tested 2200not tested T richloroethane 73°F (23°C), 30 d, i 2300not tested 2300not tested Salt Spray (5%)
95°F (35°C), 30d
1900
not tested
1500
not tested
1Hot dipped or electrodeposited. Galvanized steels may afford a wide spectrum of
performance due to the diversity of surfaces available. The ur should test to determine specific performance.
2Data reported are actual values from the lots tested and may be higher than values published elwhere in this T echnical Data Sheet.3d = days
4i = immersion