© Schaeffler Technologies AG & Co. KG, 2013
This document is to be treated confidentially. This document is a trade cret. It is given to the business partner in confidence and is protected by any applicable law. The reproduction and utilization of this document as well as the communication of its contents to others without express authorization is prohibited. Offenders will be held liable for the payment of damages. All rights rerved, especially in the event of the grant of a patent, utility model or design. In ca of doubt, the German-language original should be consulted as the authoritative text.宴会礼品
en
Gruppenstandard
Technical delivery conditions − Steel and iron
Rolling bearing steel 100Cr6
Standard quality
白茶是绿茶吗
S 130000
ICS 77.080.20; 77.140.20
2013-01-30
Descriptors: Delivery condition, steel, iron, rolling bearing steel, 100Cr6, standard quality Technische Lieferbedingungen − Stahl und Ein; Wälzlagerstahl 100Cr6; Standardqualität Deskriptoren: Lieferbedingung, Stahl, Ein, Wälzlagerstahl, 100Cr6, Standardqualität
Confidentiality rating: U for all suppliers
Superdes IS 1112 together with S 130337
Superdes part of IS 1103, IS 1109, IS 1114, IS 1117, IS 1125, IS 1126, IS 1128, IS 1152
Previous editions
S 130000: 2009-12-16, 2010-07-27, 2011-09-26 (and older) N 011400: 2000-04-01, 2000-10-01, 2004-03-24 (and older) N 011495: 2000-05-01, 2001-08-01, 2005-09-23 (and older) PL 1.001: 2001-10-31, 2006-06-14, 2006-12-04 (and older) PL 1.201: 1996-04-15, 2006-06-19, 2007-02-26
PL 1.202: 2004-04-30, 2006-06-21, 2007-02-26 (and older) PL 1.203: 2004-06-01
PL 1.218: 2001-04-30, 2006-12-04 PL 1.901A: 2001-11-30
IS 1101: 1990-01-19, 2002-01-07
IS 1102: 2001-02-06, 2001-05-21, 2001-06-16 (and older) IS 1103: 1997-10-13, 2001-12-18, 2006-06-12 (and older) IS 1104: 1989-07-27, 1993-09-15, 2002-01-26 (and older) IS 1107: 2001-11-09, 2004-01-22, 2005-09-27 (and older) IS 1109: 2004-01-20, 2004-01-28, 2005-01-26 (and older) IS 1111: 2002-03-07
IS 1112: 2002-09-30, 2002-10-08, 2002-11-27 (and older) IS 1114: 1997-10-09, 2002-04-01, 2005-05-13 (and older) IS 1117: 1999-06-15, 2002-05-15 IS 1125: 2002-05-21 IS 1126: 2002-05-21 IS 1128: 2002-05-21
IS 1152: 1999-09-09, 2003-05-01
Revisions
Compared to the 2011-09-26 edition, the following revisions have been made: Section 9 : revid, Section 13 : S for “Sections (round bars, flat bars and similar ctions) for forgings, purchad rings
made of forged blanks” was 0,003 - 0,010 %,
Section 15.1.1 : For porosity values have been added for diameter > 200 mm, Section 15.3.1 : Max. inclusion length was 10 mm,
Section “Other applicable standards, standards cited and documents ”: r evid, Editorial changes.
Page 2
S 130000: 2013-01-30
Contents
Page 10.1Sections (round bars, flat bars, sprags and similar ctions) (4)
10.2Wires (4)
10.3Tubes, rings made of tubes (5)
5g和4g有什么区别10.4Strip material (5)
10.5Rings, forged parts (5)
12.1Tubes (6)
12.2Rings (6)
15.1Internal defects (9)招贴画图片
15.1.1Internal defects of mi-finished products (9)
15.1.2Internal defects of rings and rollers (9)
15.2Microscopically determined degree of purity (10)
15.3Macroscopic non-metallic inclusions (10)
15.3.1Ultrasonic immersion test (10)
15.3.2Alternative methods (subject to agreement) (10)
Page 3
S 130000: 2013-01-30
Dimensions in mm
1 Scope of application
The delivery conditions specify the mechanical properties of mi-finished products and raw parts made of rolling bearing steel grade 100Cr6, and the designation of the as-delivered conditions.
2 Comparable with
EN ISO 683-17 100Cr6, ASTM A295 SAE 52100, JIS G 4805 SUJ2, KS D 3525 STB2, GB T 18254 GCr15
3 Material number
Comparable with B1 or 1.3505
4 Quality group
Alloyed special steel
5 Property group
Rolling bearing steel
6 Melting mode
Electric steel or LD process at the supplier’s discretion; vacuum de gasd; for comparable process approval must be obtained from the Materials Engineering departments; no Ca or Ca alloys may be added for deoxidation or inclusion inspection.
7 Casting mode
Bottom ingot casting; if continuous casting is ud, a minimum reduction ratio of 20 : 1 is preferred.
Wire for balls: Bottom ingot casting or continuous bloom casting with cross-ction
Square : ≥ 350 x 300 mm
Round : ≥ 330 mm.
Balls for constant velocity joints (at uncritical load; …CV balls“): continuous casting with a reduction ratio > 60 : 1 is permissible (a hint must be given in the order text).
8 Ud for
Rolling bearing parts and components
9 Semi-finished products
INA: TL (Technical delivery conditions)
Round bars, bright : S 130303
Round bars, hot rolled : N 01101
Round bars, hot rolled for hot forming : N 01102
Flat bars, hot rolled : N 01107
Slide plate profiles for shaft guidings : S 130316
Sprag profiles : N 01118
Wires, hot formed: S 130302 (for needles and rollers)
Wires, hot formed: S 130324 (for balls)
Wires, cold formed: S 130321 (for needles and rollers)
Wires, cold formed: S 130323 (for balls)
Strip material, cold formed : S 130337
Strip material, hot formed : S 130342
Precision steel tubes : N 01146
Tubes, amless hot rolled and peeled : N 01152
Tubes, amless hot rolled : N 01153
Rings, rolled, presd : S 130364-1 et qq.
Rings, die forged : N 01165
Drop forgings : N 01170
FAG: FPL (manufacturing-specific ordering instruction)
Page 4
S 130000: 2013-01-30
10 As-delivered conditions
A comparative list of the old and new designations of the as-delivered conditions is contained in the Appendix.入团志愿书范文800字
10.1 Sections (round bars, flat bars, sprags and similar ctions)
G annealed for cold sawing (forging)
GKZ annealed to globular cementite
GKZ+K annealed to globular cementite + cold drawn
GKZ+K+RPR annealed to globular cementite + cold drawn + crack tested
GKZ+K/SH annealed to globular cementite + cold drawn or peeled at the supplier’s discretion
GKZ+K/SH/SL+RPR annealed to globular cementite + cold drawn or peeled or ground at the supplier’s discretion + crack tested
GKZ+SH annealed to globular cementite + peeled
GKZ+SH+PO annealed to globular cementite + peeled + roller burnished
GKZ+SH+RPR annealed to globular cementite + peeled + crack tested
GKZ+SL annealed to globular cementite + ground没谱儿
GKZ+K/SH+SL annealed to globular cementite + cold drawn or peeled at the supplier’s discretion + ground GKZ+K/SH+SL+RPR annealed to globular cementite + cold drawn or peeled at the supplier’s discretion + ground + crack tested
U untreated
U+SH untreated + peeled
10.2 Wires
GKZ annealed to globular cementite
GKZ+K annealed to globular cementite + cold drawn
GKZ+LG annealed to globular cementite + slightly skin rolled
半边
GKZ+SH annealed to globular cementite + peeled
K+GKZ+LG cold drawn + annealed to globular cementite + slightly skin rolled
U untreated (wire rod)
Page 5
S 130000: 2013-01-30 10.3 Tubes, rings made of tubes
GKZ annealed to globular cementite, low stress
GKZW annealed to globular cementite, mild
GKZW+SH annealed to globular cementite, mild + peeled
GKZ+K annealed to globular cementite + cold worked
GKZ+K+G annealed to globular cementite + cold worked + final annealed
GKZ+K+SL annealed to globular cementite + cold worked + ground
GKZ+KP annealed to globular cementite + cold pilgered
GKZ+KP+SZ annealed to globular cementite + cold pilgered + final annealed (light surface oxidation permissible) GKZ+SH annealed to globular cementite + peeled
GKZ+K+GBK annealed to globular cementite + cold worked + final annealed in an oxygen-free atmosphere SOG+K+GBK specially annealed to globular cementite + cold worked + final annealed in an oxygen-free
atmosphere
SOG+KP specially annealed to globular cementite + cold pilgered
10.4 Strip material
GKZ annealed to globular cementite
GKZ+K annealed to globular cementite + cold rolled
10.5 Rings, forged parts
GKZ annealed to globular cementite, low stress
GKZ+K annealed to globular cementite + cold manufactured
U untreated
11 Mechanical properties