Effects of Design Features on Rigid Pavement Performance
The performance of rigid pavements is affected by a variety of design features, including slab thickness, ba type, joint spacing, reinforcement, joint orientation, load trans fer, dowel bar coatings, longitudinal joint design, joint alant, tied concrete shoulders ,and subdrainage . A study was made by ERES Consultants, Inc. under FHWA contract on the effects of the features on rigid pavement performance . Ninety-five pavemen tctions located in four major climatic regions were thoroughly evaluated . The following conclusions, which provide some revealing insights into pavement performance, are abstracted from the report (Smith et al., 1990a).
Slab Thickness The effect of slab thickness on pavement performance was significant.It was found that increasing slab thickness reduced transver and longitudinal cracking in all cas. This effect was much more pronounced for thinner slabs than fo rthicker slabs . It was not possible to compare the performance of the thinner slabs and the thicker slabs directly, becau the thick slabs were all constructed directly on th esubgrade and the thinner slabs were all constructed on a ba cour .
Increasing the thickness of slab did not appear to reduce joint spalling or join tfaulting . Thick slabs pl
aced directly on the subgrade, especially in wet climates an dexpod to heavy traffic, faulted as much as thin slabs constructed on a ba cour .
Ba Type Ba types, including ba/slab interface friction, ba stiffness, ba erodibility, and ba permeability, emed to have a great effect on the performance of jointed concrete pavements . The major performance indicators, which were affected by variations in ba type, were transver and longitudinal cracking, joint spalling, and faulting .
The worst performing ba type, consisted of the cement-treated or soil cement bas, which tended to exhibit excessive pumping, faulting, and cracking. This is most likely due to the impervious nature of the ba, which traps moisture and yet can brea- k down and contribute to the movement of fines beneath the slab .
The u of lean concrete bas generally produced poor performance . Large curl -ing and warping stress have been associated with slabs constructed over lean concrete bas. The stress result in considerable transver and longitudinal cracking of the slab . The poor performance of the bas can also be attributed to a bathtub design, in which moisture is trapped within the pavement cross ction .
Den-graded asphalt-treated ba cours ranged in performance from very poor to good. The fact that the types of bas were often constructed as a bathtub design contributed to their poor performance . This improper design often resulted in vere cracking, faulting, and pumping.
The construction of thicker slabs directly on the subgrade with no ba resulted In a pavement that performed marginally. The pavements were especially susceptible to faulting, even under low traffic levels.
Pavements constructed over aggregate bas had varied performance, but were generally in the fair to very good category. In general, the more open-graded the aggregate,the better the performance . An advantage of aggregate bas is that they contribute the least to the high curling and warping stress in the slab . Even though aggregate bas are not open-graded, they are more permeable and have a lower friction factor than stabilized bas .
实习总结1000字The best bas in terms of pavement performance were the permeable bas . Typical ba cours have permeabilities ranging from 0 to less than 1 ft/day (0 .3 m/day) ; good permeable bas have permeabilities up to 1000 ft/day (305 m/day) . Specific areas of concern were the high corner deflections and the low load transfer exhibited by the permeable bas . The can affect thei
镇脑宁胶囊说明书
r long-term performance, so the u of dowel bars might be required . An unexpected benefit of using permeable bas was the reduction in "D" cracking on pavements susceptible to this type of distress .
Slab Length For JPCP, the length of slabs investigated ranged from 7 .75 to 30 ft(2.4to9.1m). It was found that reducing the slab length decread both the magnitude of the joint faulting and the amount of transver cracking. On pavements with random joint spacings, slabs with joint spacings greater than 18 ft (5.5 m) experienced more transver cracking than did the shorter slabs .
For JRCP, the length of slabs investigated ranged from 21 to 78 ft (6 .4 to 23 .9 m) .Generally, shorter joint spacings performed better, as measured by the deteriorated transver cracks, joint faulting, and joint spalling . However, veral JRCP with long joint spacings performed quite well . In particular, the long jointed pavements in New Jery, which were constructed with expansion joints, displayed excellent performance .
An examination of the stiffness of foundation was made through the u of the radius of relative stiffness, f . Generally speaking, when the ratio L/E, where L is the length of slab, was greater than 5, transver cracking occurred more frequently . This
师德师风学习计划
factor was further examined for different ba types . It was found that stiffer ba cours required shorter joint spacings to reduce or eliminate transver cracking .
Reinforcement The amount of steel reinforcement appeared to have an effect in controlling the amount of deteriorated transver cracking . Pavement ctions with less than 0.1% reinforcing steel often displayed significant deteriorated transver cracking.A minimum of 0 .1% reinforcing steel is therefore recommended, with larger amounts required for more vere climate and longer slabs.
Joint Orientation Conventional wisdom has it that skewed joints prevent the application of two wheel loads to the joint at the same time and thus can reduce load-associated distress . The results from the limited sample size in this study were ambiguous, but all of the nondoweled ctions with skewed joints had a lower PSR than similar designs with perpendicular joints . The available data provide no definite conclusions on the effectiveness of skewing transver joints for nondoweled slabs . Skewed joints are not believed to provide any benefit to doweled slabs.
Load Transfer Dowel bars were found to be effective in reducing the amount of joint faulting when compared with nondoweled ctions of comparable designs. The diameter of dowels had an effect on performance, becau larger diameter bars provided better load transfer and control of faulting u
nder heavy traffic than did smaller dowels.It appeared that a minimum dowel diameter of 1 .25 in . (32 mm) was necessary to provide good performance .
Nondoweled JPCP slabs generally developed significant faulting, regardless of pavement design or climate . This effect was somewhat mitigated by the u of permeable bas. However, the ctions in this group had a much lower number of accumulated ESAL, so no definite conclusions can be drawn yet .
Dowel Bar Coatings Corrosion-resistant coatings are needed to protect dowels from the adver effects of moisture and deicing chemicals .While most of the ctions in this study did not contain corrosion-resistant dowel bars, tho that did generally exhibited enhanced performance. Very little deteriorated transver cracking was identified on the ctions. In fact, one ction in New Jery with stainless steel-clad dowel bars was performing satisfactorily after 36 years of rvice .
Longitudinal Joint Design The longitudinal joint design was found to be a critical design element.Both inadequate forming techniques and insufficient depths of joint can contribute to the development of longitudinal cracking . There was evidence of the ad vantage of sawing the joints over the u of inrts . The depth of longitudinal joints is generally recommended to be one-third of the actual, not
designed, slab thickness, but might have to be greater when stabilized bas are ud .
Joint Sealant Joint aling appeared to have a beneficial effect on performance . This was particularly true in harsh climates with excessive amounts of moisture . Preformed compression alants were shown to perform well for more than 15 years under heavy traffic.Except where "D" cracking occurred, pavement ctions containing preformed alants generally exhibited little joint spalling and were in good overall conditions.Rubberized asphalt joint alants showed good performance for 5 to 7 years.
Tied Concrete Shoulders It is generally believed that tied concrete shoulders can reduce edge stress and corner deflections by providing more lateral supports to the mainline pavement, thus improving pavement performance . Surprisingly, this study showed that, although tied concrete shoulders performed better than asphalt shoulders,many of the tied shoulders were not designed properly and actually contributed to poor performance of the mainline pavement . The tiebars were spaced too far apart ,sometimes at a spacing of 40 in.(1016 mm), and were not strategically located near slab corners to provide adequate support . In some cas, tied concrete shoulders were constructed over a stabilized den-graded ba in a bathtub design, resulting in the poor performance of mainline pavement.
Subdrainage The provision of positive subdrainage, either in the form of longitudinal edge drains or the combination of a drainage layer and edge drains, generally reduced the amount of faulting and spalling related to "D" cracking . With few exceptions, the load-associated distress, especially faulting and transver cracking, decread as the drainage characteristics improved . The overall pavement performance can be improved by using an open-graded ba or restricting the percentage of fines . A filter layer must be placed below the permeable ba, and regular maintenance of the outlets must be provided .
译文
结构特点对刚性路面性能的影响
优秀学生刚性路面的性能受种种结构特点的影响，如板厚、基层类型、接缝间距、钢筋用量、接风方向、荷载传递、传力杆涂层、纵缝设计、接缝填封料、有拉杆混凝土道肩和地下排水等。ERES咨询公司于联邦公路局（FHWA）签订合同，研究这些结构特点对刚性路面的影响。对四个主要气候区内95个路面段作了详细的评定。从研究报告（Smith等，1990a）摘录了以下结论，以便对路面性能有一透彻的理解。
一、板厚
板厚对路面性能的影响很大。发现在所有的实例中，增加板厚，是纵向和横向开裂减小。这种影响对对薄的路面板，比厚板更为明显。不可能直接将薄板的想能与厚板进行比较，因为板厚都直接铺筑在土基上，而薄板都铺筑在基层上。
增加板厚并不能减少接缝剥落及接缝错台。厚板直接铺在土基上，尤其是气候潮湿交通繁重的情况下，产生的错台同铺筑在基层上的薄板同样也很多。
二、基层类型
基层类型，包括基层与板的界面摩擦力、基层刚度、基层抗冲刷能力和基层透水性，看来对有接缝混凝土路面性能有很大影响。受各种基层类型影响的主要性能指标是横向额纵向开裂、接缝剥落和错台。
帮的成语性能最差的基层类型是水泥稳定或水泥土基层，最容易于楚翔很对唧泥、错台和开裂。这很可能是因为基层不透水，它吸收水分，易于断裂，使得板下的细颗粒发生移动。
应用贫混凝土基层，一般工作性能都很差。很大的翘曲应力是与贫混凝土基层上铺筑路面板有关系的。由于这些应力，使得面板产生很多横向和纵向的裂缝。这些基层的性能差，还可能是由于路面横截面按盆状设计，造成水分集中。
说木叶教案
密级配沥青稳定基层的性能从很差到好都有。性能低劣的原因是这些基层类型经常采用盆状设计，这种错误设计结果将产生严重的开裂、错台和唧泥。高中班主任评语
厚的面板直接铺筑在不舍基层的土基上，路面勉强合格。这些路面特别容易错台，即使交通量不大也是如此。
炒香菇的家常做法铺筑在集料基层上的路面具有不同性能，但是一般属于良好到很好等级。通常，集料开集配空隙越多。性能越好。集料基层的优点是由于基层引起的面板翘曲高应力是最小的。即使集料基层不是开集配的，也比稳定基层具有较好的透水性和较低的摩擦系数。
在路面性能方面最好的基层是透水基层。常用基层的渗透率在0至0.3m/d(1ft/d)，而好的透水基层渗透率达305m/d(1000ft/d)。需要特别考虑的