Performance improvement of GaN-bad LEDs with step stage InGaN/GaN strain relief layers in Chuanyu Jia, Tongjun Yu,* Huimin Lu, Cantao Zhong, Yongjian Sun, Yuzhen Tong,
and Guoyi Zhang
The State Key Laboratory for Mesoscopic Physics, School of Physics, Peking University, Beijing 100871, China
*tongjun@pku.edu
Abstract: The performance of nitride-bad LEDs was improved by
inrting dual stage and step stage InGaN/GaN strain relief layer (SRL)
between the active layer and n-GaN template. The influences of step stage
GaN-bad LEDs were investigated. The analysis of strain effect on
recombination rate bad k⋅p method indicated 12.5% reduction of strain in
structures. The surface morphology was improved and a smaller blue shift
in the electroluminescence (EL) spectral with increasing injection current
was obrved for LEDs with step stage SRL compared with conventional
LEDs. The output power of LEDs operating at 20mA was about 15.3mW,
incread by more than 108% by using step stage InGaN/GaN SRL, which
shows great potential of such InGaN/GaN SRL in modulating InGaN/GaN
MQWs optical properties bad on its strain relief function.
©2013 Optical Society of America
OCIS codes: (230.3670) Light-emitting diodes; (250.5590) Quantum-well, -wire and -dot
devices.
References and links
1. S. Nakamura, T. Mukai, and M. Senoh, “Candela-class high-brightness InGaN/AlGaN double-heterostructure
blue-light-emitting diodes,” Appl. Phys. Lett. 64(13), 1687–1689 (1994).
2. S. Nakamura, M. Senoh, S. Nagahama, N. Iwasa, T. Yamada, T. Matsushita, Y. Sugimoto, and H. Kiyoku,
“Room-temperature continuous-wave operation of InGaN multi-quantum-well structure lar diodes with a lifetime of 27 hours,” Appl. Phys. Lett. 70(11), 1417–1419 (1997).
3. S. Nakamura, “The roles of structural imperfections in InGaN-bad blue light-emitting diodes and lar diodes,”
Science 281(5379), 956–961 (1998).
4. Y. T. Rebane, Y. G. Shreter, B. S. Yavich, V. E. Bougrov, S. I. Stepanov, and W. N. Wang, “Light emitting
diode with charge asymmetric resonance tunneling,” Phys. Status Solidi A 180(1), 121–126 (2000).
5. T. Takeuchi, C. Wetzel, S. Yamaguchi, H. Sakai, H. Amano, I. Akasaki, Y. Kaneko, S. Nakagawa, Y. Yamaoka,
and N. Yamada, “Determination of piezoelectric fields in strained GaInN quantum wells using the quantum-confined Stark effect,” Appl. Phys. Lett. 73(12), 1691–1693 (1998).
6. J. K. Sheu, G. C. Chi, and M. J. Jou, “Enhanced output power in an InGaN-GaN multiquantum-well light-
emitting diode with an InGaN current-spreading layer,” IEEE Photon. Technol. Lett. 13(11), 1164–1166 (2001).
7. Y. Chen, T. Takeuchi, H. Amano, I. Akasaki, N. Yamada, Y. Kaneko, and S. Y. Wang, “Pit formation in GaInN
quantum wells,” Appl. Phys. Lett. 72(6), 710–712 (1998).
8. I. H. Kim, H. S. Park, Y. J. Park, and T. Kim, “Formation of V-shaped pits in InGaN/GaN multi-quantum wells
and bulk InGaN films,” Appl. Phys. Lett. 73(12), 1634–1636 (1998).
9. H. K. Cho, J. Y. Lee, G. M. Yang, and C. S. Kim, “Formation mechanism of V defects in the InGaN/GaN
multiple quantum wells grown on GaN layers with low threading dislocation density,” Appl. Phys. Lett. 79(2), 215–217 (2001).
10. S. J. Huang, Y. K. Su, C. Y. Tng, S. C. Lin, and H. C. Hsu, “Improvement of light intensity for nitride-bad
multi-quantum well light emitting diodes by stepwi-stage electron emitting layer,” Appl. Phys. Express 3(12), 122106 (2010).
11. H. C. Hsu, Y. K. Su, S. J. Huang, C. Y. Tng, C. Y. Cheng, and K. C. Chen, “Enhanced Performance of
Nitride-Bad Blue LED With Step-Stage MQW Structure,” IEEE Photon. Technol. Lett. 23, 287–289 (2011). 12. V. Ramesh, A. Kikuchi, K. Kishino, M. Funato, and Y. Kawakami, “Strain relaxation effect by nanotexturing
InGaN/GaN multiple quantum well,” J. Appl. Phys. 107(11), 114303 (2010).
#184997 - $15.00 USD Received 6 Feb 2013; revid 17 Mar 2013; accepted 21 Mar 2013; published 29 Mar 2013 (C) 2013 OSA8 April 2013 | Vol. 21, No. 7 | DOI:10.1364/OE.21.008444 | O
PTICS EXPRESS 8444
13. Q. Wang, J. Bai, Y. P. Gong, and T. Wang, “Influence of strain relaxation on the optical properties of
InGaN/GaN multiple quantum well nanorods,” J. Phys. D Appl. Phys. 44(39), 395102 (2011).
14. N. H. Niu, H. B. Wang, J. P. Liu, N. X. Liu, Y. H. Xing, J. Han, J. Deng, and G. D. Shen, “Improved quality of
InGaN/GaN multiple quantum wells by a strain relief layer,” J. Cryst. Growth 286(2), 209–212 (2006).
15. P. C. Tsai, Y. K. Su, W. R. Chen, and C. Y. Huang, “Enhanced luminescence efficiency of InGaN/GaN multiple
quantum wells by a strain relief layer and proper Si doping,” Jpn. J. Appl. Phys. 49(4), 04DG07 (2010).
16. S. J. Leem, Y. C. Shin, K. C. Kim, E. H. Kim, Y. M. Sung, Y. Moon, S. M. Hwang, and T. G. Kim, “The effect
of the low-mole InGaN structure and InGaN/GaN strained layer superlattices on optical performance of multiple quantum well active layers,” J. Cryst. Growth 311(1), 103–106 (2008).
17. T. Akasaka, H. Gotoh, T. Saito, and T. Makimoto, “High luminescent efficiency of InGaN multiple quantum
wells grown on InGaN underlying layers,” Appl. Phys. Lett. 85(15), 3089–3091 (2004).
18. C. H. Jang, J. K. Shey, C. M. Tsai, S. J. Chang, W. C. Lai, M. L. Lee, T. K. Ko, C. F. Shen, and S. C. Shei,
“Improved performance of GaN-Bad blue LEDs with the InGaN inrtion layer between the MQW active layer and the n-GaN cladding layer,” IEEE J. Quantum Electron. 46(4), 513–517 (2010).
19. R. M. Lin, Y. H. Lin, C. H. Chiang, M. J. Lai, Y. L. Chou, Y. C. Lu, S. Y. Kuo, B. R. Fang, and M. C. Wu,
“Inrting a low-temperature n-GaN underlying layer to parate nonradiative recombination centers improves the luminescence efficiency of blue InGaN/GaN LEDs,” Microelectron. Reliab. 50(5), 679–682 (2010).
20. S. L. Chuang, “Optical gain of strained wurtzite GaN quantum-well lars,” IEEE J. Quantum Electron. 32(10),
1791–1800 (1996).如何拼好魔方
21. H. M. Lu and G. X. Chen, “Design strategies for mitigating the influence of polarization effects on GaN-bad
multiple quantum well light-emitting diodes,” J. Appl. Phys. 109(9), 093102 (2011).
22. T. Kuroda and A. Tackeuchi, “Influence of free carrier screening on the luminescence energy shift and carrier
lifetime of InGaN quantum wells,” J. Appl. Phys. 92(6), 3071–3074 (2002).
1. Introduction
III-nitride-bad optoelectronic devices such as light emitting diodes (LEDs), and lar diodes (LDs) have been experiencing a rapid technology progress in recent years, and are now beginning to be applied for many commercial areas such as full-color displays, traffic lights, optical storage, solid-stat
e lighting, and medical applications [1–3]. The optoelectronic devices normally employ an InGaN/GaN multiple quantum wells (MQWs) as the active layer, however, its electron capture rate is low due to the much smaller effective mass and higher corresponding thermal velocity of electrons than of holes [4], this results in the leakage of electrons to the p-GaN and harms the radiative recombination efficiency. Besides, a large lattice and thermal mismatch exits between InGaN and GaN, so there is large strain between the InGaN/GaN active layer and underlying n-GaN template. The strain can generate a large piezoelectric field in the MQW region [5], and this piezoelectric field-induced quantum-confined stark effect (QCSE) leads to a spatial paration of electrons and holes. For this reason, the radiative recombination efficiency of the MQWs will be significantly reduced [6]. Furthermore, strain in MQWs is believed to act as a driving force for the formation of the V-pits [7–9], which can make interface loss abruptness between periods within the MQW Several attempts have been made to enhance the electron capture rate of the active region and relea the residual strain in InGaN/GaN MQWs. The electron blocking layers (EBL), have been induced and studied for improving the emission of InGaN/GaN LEDs. Although nanostructures have been approved to be effective in strain relaxation, complicated process need to improve the compatibility in LED production. One of the practical approaches is to introduce an additional layer such as InGaN/GaN short period superlattices (SPS) [14–16], InGaN layer and InGaN/GaN MQW layer [17,18], or low-te
梦见红衣服mperature (LT) n-GaN layer [19], between the n-type GaN and the InGaN/GaN active layer. Studies have revealed that such inrtion layers can be regarded as the lattice-mismatch buffer between the underlying n-GaN and overlying QWs, which can relea the residual strain in MQWs layer, reduce the V-pits density in MQWs, improve the crystal quality of InGaN/GaN MQWs, enhance electron capture rate of the active layer and improve the current spreading in LED. As a result, the quantum efficiency and the output power of LED can be enhanced. However, a comprehensive mechanism involved in every well of the strain relief layer (SRL) has not been discusd in detail, nor has the structure been optimized. In this work, we managed to reduce the strain of InGaN/GaN MQWs by inrting a step stage SRL between n-GaN and MQWs,
#184997 - $15.00 USD Received 6 Feb 2013; revid 17 Mar 2013; accepted 21 Mar 2013; published 29 Mar 2013 (C) 2013 OSA8 April 2013 | Vol. 21, No. 7 | DOI:10.1364/OE.21.008444 | OPTICS EXPRESS 8445
in which the well nearer the n-type GaN has shallower depths. The strain effect in MQW
were evaluated by comparing calculated emission spectra using effective mass model bad on k⋅p method and measured luminescence properties. Compared with a fixed indium concentration InGaN/GaN SRL, this step stage SRL further improved the crystal quality and
enhanced the electron capture rate of the active region becau of the gradual change of lattice constant in the emitter layer, more greatly modified the luminescence properties of InGaN/GaN MQWs.
2. Experiment
All the InGaN-LED samples in this work were grown on (0001) sapphire substrate using a
low pressure metal organic chemical vapor deposition (LP-MOCVD) system. Trimethylgallium (TMGa), trimethylindium (TMIn), and ammonia (NH3) were ud as precursors. Silane (SiH4) and biscyclopentadienymagnesium (Cp2Mg) were ud as the n-dopant and p-dopant source. For reference, InGaN/GaN LED without SRL were also grown. All the LED structures were consisted of a 30-nm-thick GaN nucleation layer grown at 550°C, followed by a 2-μm-thick undoped GaN layer grown at 1050°C, a 4-μm-thick Si doped n-type GaN layer with a carrier concentration of 5 × 1018cm-3 grown at 1050°C, five pairs of In0.15Ga0.85N/GaN MQWs active layer grown at 750°C, 5 periods of p-Al0.15Ga0.85N(2nm)/GaN(2nm) superlattices EBL and a 150-nm-thick Mg-doped p-GaN layer grown at 980°C, as shown in Figs. 1(a) and 1(b). SRLs were sandwiched between n-GaN and InGaN/GaN MQWs. First, a kind of fixed In content SRL which has 5 periods of 2nm In0.08Ga0.右造句
92N well and 3nm GaN barrier were grown and shown as Fig. 1(c). Another short period superlattice-like SRL structure with step stage indium content consists of 5 periods of 2nm thick InGaN well and 3nm thick n-GaN barrier. Stepwi indium doped MQW structures are obtained by controlling the flow rate of TMIn during growth, the In content in each well layer is t to be 0.01, 0.04, 0.07, 0.1, 0.13 as illustrated in Fig. 1(d). After growth, the LED chips were fabricated by regular chip process with indium tin oxide current spreading layer and Ni/Au contact metal, and the size of mesa is 350 × 350μm2. In order to investigate the surface morphology of MQWs by atom force microscopy (AFM), three samples without the p-AlGaN/GaN EBL and the p-GaN layer were also grown, denoted as single stage MQW, dual stage MQW and step stage MQW, and LED samples correspondingly called as single stage LED, dual stage LED and step stage LED. Room temperature electro-luminescence (EL) characteristics, current-voltage (I-V), and output power-current (L-I) characteristics of LEDs were evaluated at various injection currents.
Fig. 1. (a) The schematic diagram of LED with InGaN/GaN SRL; Illustration of TMIn flow
rate for controlling the indium composition during the growth of (b) single stage MQW, (c)
dual stage MQW and (d) step stage MQW.
3. Results and discussion
The piezoelectric polarization induced by strain effect can change directly the emission properties of GaN-bad MQW LEDs. So, the strain effect in MQW can be evaluated by
#184997 - $15.00 USD Received 6 Feb 2013; revid 17 Mar 2013; accepted 21 Mar 2013; published 29 Mar 2013 (C) 2013 OSA8 April 2013 | Vol. 21, No. 7 | DOI:10.1364/OE.21.008444 | OPTICS EXPRESS 8446
comparing calculated emission spectra using effective mass model bad on k⋅p method and measured luminescence properties [20, 21]. Figure 2(a) gives the polarization field in well layers and corresponding carrier overlap percentage varying with in-plane compressive strain for In0.15Ga0.85N/GaN MQWs grown along the (0001) direction. The polarization filed increas as in-plane compressive strain that leads to the decline of overlap percentage of electrons and holes. As a result, the emission from MQWs enhances when compressive strain in well layers reduces. Simultan
eously, the emission peak shifts toward shorter wavelength due to the decrea of polarization field. Figure 2(b) gives the measured PL spectra of the single stage LED, dual stage LED and step stage LED. In order to evaluate the strain effect in such different MQWs, the spontaneous emission spectra of MQWs with different in-plane compressive strain are calculated and shown in Fig. 2(c). By comparing the calculated and measured emission peak, it is concluded that the in-plane compressive strain is about 0.016 for conventional single stage In0.15Ga0.85N/GaN without SRL that results in 2.27MV/cm polarization field and 14% carrier overlap from Fig. 2(a). The overlap percentage of electrons and holes increas to 19% when the strain reduces to 0.014 by using step stage SRL. As a result, the spontaneous emission intensity can be enhanced by inrting InGaN/GaN SRL, especially the step stage SRL. However, the peak intensity step stage MQWs increas more than 100% as compared to single stage MQW in measured results, more obviously than that in calculated results. Except for the decrea of polarization field, the improvement of crystal quality from reduction of the strain in MQWs with InGaN/GaN SRL should be also responsible for the improvement of the PL properties.
花头像微信
吴亦凡歌曲
Fig. 2. (a) Strain effect on polarization field and overlap percentage of electrons and holes (b)
measured PL spectra at room temperature and (c) calculated spontaneous emission spectra for
InGaN/GaN MQW
Figure 3 shows the HRXRD 2theta/omega scans of (0002) plane in single stage LED, dual stage LED and step stage LED for comparison. Single stage MQW structure has well defined satellite diffraction peaks up to the fourth order, while both the dual stage MQW and the step stage MQW structures give satellite peaks up to the fifth order. This means good structure quality of the MQWs and the abrupt interfaces between the barriers and wells. Furthermore, it is obrved that the satellite peaks in step stage LED and dual stage LED is clearer than that in single stage LED, indicating that the inrted InGaN/GaN SRL acts as a buffer modulating the strain in the active region and the underlying GaN and overlaying layers are of better quality.
5 × 5μm2 AFM images of InGaN/GaN MQWs without SRL, with dual stage SRL and step stage SRL
are shown in Fig. 4. The large and den V-shape pits caud by the threading dislocation or stacking faults as reported in previous studies are obrved in the sample without SRL as Fig. 4(a). The density and root mean square (RMS) roughness of pits are in the range of 4-5 × 108cm-2 and 0.53 nm, respectively. In contrast, the values for dual stage SRL sample in Fig. 4(b) are smaller in the range of 1-2 × 108cm-2 and 0.
6 nm, respectively, and further reduced to 2-4 × 107cm-2 and 0.23 nm for step stage SRL sample in Fig. 4(c). It has been reported that the strain is a primary cau of the formation of V-pits [7–9]. Then, obvious decrea of V-pits in step stage MQW should be due to the reduced strain in InGaN active layers. Less V-pits in the MQW also benefit good interface abruptness between periods within the MQW stack, so that step stage MQW shows better crystal quality as compared
#184997 - $15.00 USD Received 6 Feb 2013; revid 17 Mar 2013; accepted 21 Mar 2013; published 29 Mar 2013 (C) 2013 OSA8 April 2013 | Vol. 21, No. 7 | DOI:10.1364/OE.21.008444 | OPTICS EXPRESS 8447
with dual stage MQW and MQW without SRL, and improved performance of step stage LED can be expected.
Fig. 3. The HRXRD 2theta/omega scans of (0002) plane in single stage LED, dual stage LED关于拼搏的诗句
校园新闻and step stage LED.
毕业季图片
Fig. 4. 5 × 5μm2 AFM images of InGaN/GaN MQWs (a) without SRL, (b) with dual stage
SRL and (c) with step stage SRL.
The EL spectra of InGaN/GaN MQW LEDs without SRL, with step stage SRL were measured with increasing injection current. A large blue shift of the emission peak about 6.4nm from 452.8nm to 446.4nm was obrved for LEDs without SRL when the injection current incread from 1 to 20 mA, shown in Fig. 5(a). A smaller blue shift of the emission peak about 4.2nm from 451.6nm to 447.4nm for dual stage LEDs, and much smaller shift 2.2nm from 444.6nm to 442.4nm for step stage LEDs are shown in Figs. 5(b) and 5(c). Blue-shift could be caud by the band-filling and QCSE [22]. However, the shift due to band-filling effect can be excluded becau the highest injection current is only 20mA in this EL spectra measurement. Then, it ems as Leem et al. concluded that blue-shift of emission is due to the strain between the GaN epilayer and MQW [16]. Then, a larger blue-shift is the clear evidence that LEDs without SRL suffer the stronger QCSE than tho with step stage SRL.
Fig. 5. The EL spectra of InGaN/GaN MQW LEDs (a) without SRL, (b) with dual stage SRL
and (c) with step stage SRL, the spectra were measured with increasing injection current from
1mA to 20mA.
#184997 - $15.00 USD Received 6 Feb 2013; revid 17 Mar 2013; accepted 21 Mar 2013; published 29 Mar 2013 (C) 2013 OSA8 April 2013 | Vol. 21, No. 7 | DOI:10.1364/OE.21.008444 | OPTICS EXPRESS 8448
Output powers as functions of injection current for LEDs are shown in Fig. 6. The 20mA
output power of the single stage LED, dual stage LED and step stage LED are 7.3mW, 12.7mW and 15.2mW, respectively. The step stage InGaN/GaN underlying layer helped
LEDs performance improvement about 108%, and delivered further improvement approximately 20
% compared to dual stage MQW LEDs at 20 mA, and such output power enhancement was even enlarged to 112% and 30% at high injection 300mA in our other experiments. Carrier involved in radiative recombination centers and the carrier injection efficiency could be markedly improved by inrting the short period InGaN/GaN superlattice-like SRL structure.
Fig. 6. Output powers as functions of injection current for single stage, the dual stage and step
stage MQW LED.
4. Conclusion
The performance of nitride-bad LEDs was improved by inrting dual stage and step stage InGaN/
GaN SRL between the active layer and n-GaN template as compared with MQWs without SRL. The influences of step stage and dual stage InGaN/GaN SRL on the structure, electrical and optical characteristics of GaN-bad LEDs were investigated. With the analysis of strain effect on recombination rate bad k⋅p method, it is estimated that the strain in InGaN/GaN MQWs was reduced about 12.5% by inrting step stage InGaN/GaN superlattice-like SRL. The surface morphology was improved and a smaller blue shift in the electroluminescence (EL) spectral with increasing injection current was also obrved. The output power of LEDs with SRL at 20mA was incread by more than 108%. The asymmetric step stage InGaN/GaN SRL is believed to be effective to modulate strain and improve the luminous properties of InGaN/GaN MQWs LEDs.
Acknowledgments
This work is supported by the National Key Basic Rearch Program of China under Grant
No. 2013CB328705, 2011CB301900, and 2011CB013100, the National High-Tech Rearch. and Development Program of China under Grant No 2011AA03A103, and the National Natural Science Foundation of China under Grant No. 61076012, 61076013 and 61204054.
#184997 - $15.00 USD Received 6 Feb 2013; revid 17 Mar 2013; accepted 21 Mar 2013; publishe
d 29 Mar 2013 (C) 2013 OSA8 April 2013 | Vol. 21, No. 7 | DOI:10.1364/OE.21.008444 | OPTICS EXPRESS 8449