塑膠材料特性total: 9 pages
1. 分類
一般塑膠材料可區分為熱硬化材料(thermotting plastics)和熱可塑性材料
(thermoplastics) 等二類.也可按結晶性分結晶性材料(crystalline polymer)和非結晶性材料(amorphous polymer).按用途來分為通用塑料(general plastics)和工程塑料(engineering plastics).
2. 塑料的各種特性:
塑膠(Plastics)有物理性質、機械性質、電气性質、化學性質等.
(1) 物理性質:
(a) 熱性質:
●比熱(specific heat):
●熱膨脹系數(coefficient of thermal expansion):.
●熔化點(Melting point t m):
●熱變形溫度(heat distortion temperature):
另外還有熱傳導性(thermal conductivity) 、溫度傳導率(thermal conductivity) 、玻
璃体轉移點等(glass transition point, T g)
(b) 容積、尺寸精度有關的特性值
●比重(Specific gravity)
●成型收縮率(Molding shrinkages)
●老化及加熱處理的尺寸穩定性(Dimension stability)
●成型品的表面粗糙度(Surface roughness of moldings)
(2) 機械性質:
●抗拉強度(Tensile strength)
●壓搞抗強度(Compression strength)
●彎曲強度(Bending strength)
●剪切強度(Direct shear strength)
●扭抗強度(Torsion shear strength)
●沖擊強度(Impact strength)
●表面硬度(Surface hardness)
●蠕變特性(Creep properties)
●疲勞特性(Fatigue properties)
(3) 電气性質
●電阻(Electric resistance)
●介定強度(Dielectric strength)
●耐電孤性(Dry arc resistance)
(4) 成型工藝特性
●成型溫度(Molding temperature)和樹脂溫度(Polymer temperature)
●模具溫度(Mold temperature)
好仔仔●注射壓力(Injection pressure)和鎖摸壓力(Mold clamping pressure.)
●注射速率(Injection speed)和射出時間(Injection time)
(5) 耐化學特性
略
(6) 塑膠的常用簡易鑒別方法
塑膠鑒別前，最好能熟悉各種塑膠的相關特性.
常用的鑒別方法主要有：燃燒特性，是否溶于溶劑、比重、硬度.
尤以燃燒特性，是否浮于水面等方法最為通用.
燃燒塑膠片來觀察其燃燒難易、冒湮情況、臭氣、是否軟化，可以簡單判別. 燃燒時，對溶融、軟化部分趁熱用鑷子夾住拉伸，熱塑性塑料會被拉伸成纖維狀，熱固性塑料則不會.
熱固性樹酯若在火焰上烤時不燃不軟化而膨脹成白體，或者裂開的話，那就是尿素類樹脂.
有關各種塑烊的燃燒難易，冒湮，臭氣等情況見附表.另現有常用樹酯中，通常只有PE,PP 等塑膠可浮在水面上，有關塑料的具體鑒別步驟可見附表二.
3.常用塑料主要性能表
聚氯乙烯和氯乙烯-醋酸乙烯共聚樹脂
聚乙烯(PE) 性能(property) 單位(unit) 硬質
軟質\無填料
軟質有填料
高密度
低密度
乙烯-醋酸乙
烯共聚樹脂
聚丙烯(PP) ABS 樹脂
密度(density)
g/cm 3 1.35~1.45 1.16~1.45 1.3~1.7 0.941~0.965 0.910~0.920 0.93 0.90~0.915 1.01~1.15
吸水率(molding
shrinkages) % 0.07~0.4 0.15~0.75 0.5~1.0 <0.01 <0.01 0.04 <0.01 0.1~0.8
拉伸強度
真正瑞士手表
(tensile
strength)
MPa 34.5~62.03 10.29~24.11 6.89~24.11 21.36~37.93 6.86~15.88 5.49~13.82 33.03~41.36 16.56~62.03 伸長率(tensile
elongation) % 2.0~40.0 200~450.0 200~400.0 15~100 90~650 300~700 200~700 10~140
彎曲強度
(bending
ps怎么改数字
strength)
MPa 68.89~110.25 68.60 20.68~24.79 41.36~55.08 24.79~93.00 壓縮強度
(compression strength)
MPa 55.08~89.57
6.20~11.76 6.89~12.45 22.05 1
7.25~17.75 沖擊強度
(impact
strength)
Kj/m 2 0.86~42.9 因牌號和增塑劑而不同 1.7~4.2 不破壞 不破壞 1.07~4.3 1.5~25.7 硬度(hardness) 邵氏(洛氏)
D65~85 A50~100 A50. ~100 D60~70 D27~36 (R85~110) (R30~118)
幼儿园发展建议
比熱熔(specific heat) J/kg.K 837.36~1172.30 1256.04~2093.40 1256.04~2093.40 2302.74 2302.74 2219.00 2009.66
1381.64~167
4.72 熱變形溫度
(heat
distortion), 0
C 1.813 MPa 0.45 MPa 54~79
57~82 60~82 40~50 99~116 65~107 體積電阻率(volume
resistivity)(濕度50%230C)
Ω.cm >1016 1011~1015 1011~1014 1015~1016 <1016 2.4X109 6.5X1016 5X1012~1017
介電強度(dielectric
strength) (3.2mm 厚) K V/mm 17~52 12~40 10~32 17.7~19.7 18.1~27.5 17. ~21.5 19.7~26.0 12.2~16.0
耐電弧性(dry
arc resistance)
S 60~80 135~160 185 47~80
聚苯乙烯樹脂
聚甲基丙烯酸甲醋樹脂(PPMA)
性能(property)
單位(unit)
一般型
抗沖型
耐化學耐熱
20~30%玻璃纖維
增強
聚甲基丙烯酸
與笨乙烯共聚
與a-甲基笨乙烯共聚
密度(density)
猴子怎么出装拒绝的英文g/cm 3 1.04~1.065 0.98~1.10 1.05~1.11 1.20~1.33 1.17~1.20 1.12~1.16 1.16
吸水率(molding
shrinkages)
% 0.03~0.05 0.1~0.3 0.05~0.4 0.05~0.07 0.3~0.4 0.2
0.2 拉伸強度(tensile
strength)
MPa 34.50~62.03 13.72~46.84 44.79~137.79 75.75~103.39 48.22~75.75 62.03
34.50~62.03
伸長率(tensile
elongation)
% 1.0~2.5 5~80 1.4~2.5 0.75~1.3 2~10 4~5 >15~50
彎曲強度(bending
strength)
MPa 60~96.43 34.40~68.89 68.89~117.11 103.39~130.93 89.57~117.11 100.64~130.93 55.08~89.57
壓縮強度
(compression
strength)
MPa 79.28~110.25 27.54~61.94 82.32~110.15 96.43~117.11 80.71~123.97 75.75~103.39 27.54~96.43 沖擊強度(impact
strength) Kj/m 2 0.54~0.86 1.1~23.6 0.75~13 0.86~0.64 0.64~1.1 0.75~11 0.64
硬度(hardness)
邵氏(洛氏) (M65~80) (M20~80) (M65~90) (M70~95) (M85~105) M70~85 (R99~120)
比熱熔(specific heat) J/kg.K 1339.78 1339.78~1465.38 1339.78~1465.3
8 962.96~1130.44 1465.38
熱變形溫度(heat distortion), 0
C 1.813 MPa 0.45 MPa 65~96 64~92.5 82~112 103 68~99 74~107 85~99 108~112
127~131 體積電阻率(volume
resistivity)(濕度50%230C)
Ω.cm >1016 >1016 1013~1017 3.2~3.7X1016 >1014 >1016
介電強度(dielectric
strength)
(3.2mm 厚)
K V/mm 19.7~27.5 1.77~21.6 15.7~17.7 18.7 耐電弧性(dry arc
resistance)
S 60~80 20~100 60~135 25~40
聚脂
聚氟樹脂
聚碳酸酯(PC)
性能(property)
單位(unit)
PETP PBTP 聚四氟乙烯
聚三氟乙烯 聚偏二氯乙烯
四氟乙烯和六
氟丙烯共聚 無填料
10~40%玻璃纖維增強
密度(density)
g/cm 3 1.34~1.39 1.31~1.38 2.1~2.2 2.1~2.2 1.76~1.77 2.14~2.17 1.2
1.24~1.5
吸水率(molding
shrinkages)
% 0.1~0.2 0.02~0.09 0.01 0.01 0.01 0.01 0.15 0.07~0.10
拉伸強度(tensile
strength)
MPa 18.31~72.03 56.25 13.82~30.97 30.97~41.36 4.80
18.62~21.36 55.08~65.46 96.43~137.79
伸長率(tensile
elongation)
% 3~300 50~300 200~400 30~350 100~300 250~330 60~100 0.9~2.2
彎曲強度(bending
strength)
MPa 96.04~123.48 82.32~114.56 50.96~64.09 75.75~89.57 154.35~206.68
壓縮強度
(compression
strength)
MPa 75.46~102.90 59.00~99.47 11.76 31.56~50.76 68.89 87.87 110.64~130.93 沖擊強度(impact
strength) Kj/m 2 1.2~3.5 4.3~5.4 6.4 5.4~5.8 7.5 2.57~3.57
硬度(hardness)
邵氏(洛氏) (M94~101) (M68~98) D50~65 (R75~95) D80 (R25) (M70,R118) (M80~90)
比熱(specific
heat)
J/kg.K 1046.7 921.10 1381.64 1256.04
熱變形溫度(heat distortion), 0C 1.813 MPa
0.45 MPa 121 126 149 132~143 295~315
體積電阻率(volume
resistivity) (濕度50%230C)
Ω.cm 1015~1016 >1018 1.2X1018 1014 >1018 2.1X1016 1.4~1.52X1015
介電強度(dielectric
strength)
(3.2mm 厚)
侍奉的意思K V/mm >35 18.8 19.7~23.6 10.2 19.7~23.6 15.7 18.7 耐電弧性(dry arc
resistance)重要近义词
S 75~192 >200 >360 >165 10~120 7~120
聚甲(POM) 聚胺樹脂(PA)
性能(property) 單位(unit)
均聚共聚聚風(PSF) 聚苯醚(PPO)
尼龍-6 尼龍-66 尼龍-9
密度(density) g/cm3 1.425 1.41 1.24 1.18
1.13~1.16 1.09~1.14 1.05
吸水率(molding shrinkages) % 0.25 0.22 0.22 0.13 1.6
0.4~1.5
拉伸強度(tensile strength) MPa 68.60 60.37 69.97 65.46
70.27~82.71 61.74~82.32 56.84~63.70
伸長率(tensile
elongation)
% 注射15, 擠壓75 60~75 50~100 50~100 25~320 25~200
彎曲強度(bending
strength)
MPa 96.04 8.18 105.84 96.43 55.08~96.04 85.75~96.04 78.40~83.30 壓縮強度
(compression
strength)
MPa 123.48 109.76 95.35 82.71 46.16~85.95 49.59~89.57
沖擊強度(impact strength) Kj/m2
注射7.6, 擠壓
12.5
6.5~
7.6 2.6 3.2~4.1
2.1~11.8 2.1~4.3
硬度(hardness) 邵氏(洛氏) (M94, R120) (M78~80) (M69, R120)
(M69,
R118~120)
(103~118) (R108~118)
比熱 (specific
heat)
J/kg.K
熱變形溫度(heat distortion), 0C 1.813 MPa
0.45 MPa
170 158 174
175~185
180~190
60~70
149~185
66~86
182~184
體積電阻率
(volume resistivity)(濕度50%230C) Ω.cm 6X1014 1
X1014 1016 1016~1013
45X1013~4X10
14
1012~1015 5.5 X 1014
介電強度
(dielectric strength) (3.2mm厚) K V/mm
18.6 19.7 16.7 16~20.5 17.3~20.2 15.1~18.5 >15