V alox* Resin 357
A sia Pacific: COMMERCIAL
PBT + PC, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.
T YPICAL PROPERTIES ¹
TYPICAL VALUE
UNIT
STANDARD
M ECHANICAL
T ensile Stress, yld, Type I, 50 mm/min 48M Pa A STM D 638T ensile Stress, brk, Type I, 50 mm/min 48M Pa A STM D 638T ensile Strain, yld, Type I, 50 mm/min 5%A STM D 638T ensile Strain, brk, Type I, 50 mm/min 110%A STM D 638T ensile Modulus, 5 mm/min
2020M Pa A STM D 638F lexural Stress, yld, 1.3 mm/min, 50 mm span 83M Pa A STM D 790F lexural Stress, brk, 1.3 mm/min, 50 mm span 83M Pa A STM D 790F lexural Modulus, 1.3 mm/min, 50 mm span 2060M Pa A STM D 790H ardness, Rockwell R
117-A STM D 785I MPACT
Izod Impact, unnotched, 23°C 3204J /m A STM D 4812 Izod Impact, notched, 23°C 534J /m A STM D 256 Izod Impact, notched, -30°C 153J /m A STM D 256 Gardner,  23°C
43J A STM D 3029 Modified Gardner, 23°C李宁牌
43J A STM D 3029 Instrumented Impact Total Energy, 23°C 35J A STM D 3763 Izod Impact, notched 80*10*4 +23°C 45k J/m²I SO 180/1A  Izod Impact, notched 80*10*4 -30°C
10k J/m²I SO 180/1A  Charpy  23°C, V-notch Edgew 80*10*4 sp=62mm
45k J/m²I SO 179/1eA T HERMAL
V icat Softening Temp, Rate B/50
134°C A STM D 1525H DT, 0.45 MPa, 6.4 mm, unannealed 138°C A STM D 648H DT, 1.82 MPa, 6.4 mm, unannealed 99
°C A STM D 648 CTE, -40°C to 40°C, flow 9.18E-051/°C A STM E 831 CTE, -40°C to 40°C, xflow 8.4E-051/°C A STM E 831 CTE, 60°C to 138°C, flow 1.24E-041/°C A STM E 831 CTE, -40°C to 40°C, flow
7.2E-05
1/°C
I SO 11359-2
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS AND PRODUCTS OF THE BUSINESSES MAKING UP THE SABIC INNOVATIVE PLASTICS 1) T ypical  values only. Variations  within  normal tolerances are  possible for vario colours.All values  are measured at least after 48 hours s torage at 230C/50% relative humidity.
All properties, except the melt volume rate are measured on injection m oulded samples.All samples are prepared according to ISO 294.
2) O nly typical data for material lection purpo.Not to be ud for p art or tool design.
3) T his rating is not intended to reflect hazards prented by this or any o ther material under actual fire conditions.4) O wn measurement according to UL.
5) Measurements made from laboratory test coupon.  Actual shrinkage may vary outside of range due to
篆书体
differences in processing conditions, equipment, part geometry and tool design.  It is recommended that mold  shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
Source, GMD, Last Update:11/09/2009
COMPANY, ITS SUBSIDIARIES AND AFFILIATES ("SABIC IP"), ARE SOLD SUBJECT TO SABIC IP' S STANDARD CONDITIONS OF SALE, WHICH ARE INCLUDED IN THE APPLICABLE DISTRIBUTOR OR OTHER SALES AGREEMENT, PRINTED ON THE BACK OF ORDER ACKNOW
LEDGMENTS AND INVOICES, AND AVAILABLE UPON REQUEST.  ALTHOUGH ANY INFORMATION, RECOMMENDATIONS, OR ADVICE
CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SABIC IP MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED,  (I) THAT THE RESULTS DESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (II) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SABIC IP MATERIALS, PRODUCTS, RECOMMENDATIONS OR ADVICE.  EXCEPT AS PROVIDED IN SABIC IP' S STANDARD CONDITIONS OF SALE, SABIC IP AND ITS REPRESENTATIVES SHALL IN NO EVENT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS OR PRODUCTS DESCRIBED HEREIN.Each ur bears full responsibility for making its own determination as to the suitability of SABIC IP' s materials, products, recommendations, or advice for its own particular u.  Each ur must identify and perform all tests and analys necessary to assure that its finished parts incorporating SABIC IP materials or products will be safe and suitable for u under end-u conditions.  Nothing in this or any other document, nor any oral
recommendation or advice, shall be deemed to alter, vary, superde, or waive any provision of SABIC IP' s Standard Conditions of Sale or this Disclaimer, unless any such modification is specifical
ly agreed to in a writing signed by SABIC IP.  No statement contained herein concerning a possible or suggested u of any material, product or design is intended, or should be construed, to grant any licen under any patent or other intellectual property right of SABIC Innovative Plastics Company or any of its subsidiaries or affiliates covering such u or design, or as a recommendation for the u of such material, product or design in the infringement of any patent or other
V alox* Resin 357
A sia Pacific: COMMERCIAL
T YPICAL PROPERTIES ¹
TYPICAL VALUE UNIT STANDARD
T HERMAL
波斯战象CTE, -40°C to 40°C, xflow
8.4E-051/°C I SO 11359-2V icat Softening Temp, Rate B/50145°C I SO 306V icat Softening Temp, Rate B/120
150°C I SO 306H DT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 84°C I SO 75/Af R elative Temp Index, Elec
120°C U L 746B R elative Temp Index, Mech w/impact 120°C U L 746B R elative Temp Index, Mech w/o impact
140°C U L 746B P HYSICAL
S pecific Gravity 1.34-A STM D 792S pecific Volume
0.75c m³/g A STM D 792W ater Absorption, 24 hours
0.08%A STM D 570M old Shrinkage, flow, 3.2 mm (5)
1 - 1.4%S ABIC Method M old Shrinkage, flow, 0.75-2.3 mm (5)0.8 - 1.1%S ABIC Method M old Shrinkage, flow, 2.3-4.6 mm (5)1 - 1.4%S ABIC Method M old Shrinkage, xflow, 0.75-2.3 mm (5)0.9 - 1.3%S ABIC Method M old Shrinkage, xflow, 2.3-4.6 mm (5)1.
2 - 1.6%
S ABIC Method  Melt Flow Rate, 250°C/5.0 kgf 9.6g /10 min A STM D 1238D ensity
1.34g /cm³I SO 1183 Water Absorption, (23°C/sat)
0.5%I SO 62 Moisture Absorption (23°C / 50% RH)0.15%
I SO 62 Melt Volume Rate, MVR at 250°C/5.0 kg
8c m³/10 min I SO 1133E LECTRICAL
V olume Resistivity
>1.2E+16O hm-cm A STM D 257D ielectric Strength, in air, 3.2 mm
18.5
k V/mm
A STM D 149
Source, GMD, Last Update:11/09/2009
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS AND PRODUCTS OF THE BUSINESSES MAKING UP THE SABIC INNOVATIVE PLASTICS COMPANY, ITS SUBSIDIARIES AND AFFILIATES ("SABIC IP"), ARE SOLD SUBJECT TO SABIC IP' S STANDARD CONDITIONS OF SALE, WHICH ARE INCLUDED IN THE APPLICABLE DISTRIBUTOR OR OTHER SALES AGREEMENT, PRINTED ON THE BACK OF ORDER ACKNOWLEDGMENTS AND INVOICES, AND AVAILABLE UPON REQUEST.  ALTHOUGH ANY INFORMATION, RECOMMENDATIONS, OR ADVICE
CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SABIC IP MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED,  (I) THAT THE RESULTS DESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (II) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN INCORPORATING SABIC IP MATERIALS, PRODUCTS, RECOMMENDATIONS OR ADVICE.  EXCEPT AS PROVIDED IN SABIC IP' S STANDARD CONDITIONS OF SALE, SABIC IP AND ITS REPRESENTATIVES SHALL IN NO EVENT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS OR PRODUCTS DESCRIBED HEREIN.Each ur bears full responsibility for making its own determination as to the suitability of S
ABIC IP' s materials, products, recommendations, or advice for its own particular u.  Each ur must identify and perform all tests and analys necessary to assure that its finished parts incorporating SABIC IP materials or products will be safe and suitable for u under end-u conditions.  Nothing in this or any other document, nor any oral
recommendation or advice, shall be deemed to alter, vary, superde, or waive any provision of SABIC IP' s Standard Conditions of Sale or this Disclaimer, unless any such modification is specifically agreed to in a writing signed by SABIC IP.  No statement contained herein concerning a possible or suggested u of any material, product or design is intended, or should be construed, to grant any licen under any patent or other intellectual property right of SABIC Innovative Plastics Company or any of its subsidiaries or affiliates covering such u or design, or as a recommendation for the u of such material, product or design in the infringement of any patent or other 1) T ypical  values only. Variations  within  normal tolerances are  possible for vario colours.All values  are measured at least after 48 hours s torage at 230C/50% relative humidity.
All properties, except the melt volume rate are measured on injection m oulded samples.All samples are prepared according to ISO 294.一年级数学上册
2) O nly typical data for material lection purpo.Not to be ud for p art or tool design.
3) T his rating is not intended to reflect hazards prented by this or any o ther material under actual fire conditions.4) O wn measurement according to UL.
5) Measurements made from laboratory test coupon.  Actual shrinkage may vary outside of range due to为什么会长灰指甲
differences in processing conditions, equipment, part geometry and tool design.  It is recommended that mold  shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
梦见捡到一个婴儿
V alox* Resin 357
A sia Pacific: COMMERCIAL
T YPICAL PROPERTIES ¹
TYPICAL VALUE UNIT STANDARD
E LECTRICAL
D ielectric Strength, in oil, 1.6 mm 25.2k V/mm A STM D 149
D ielectric Strength, in oil, 3.2 mm 18.5k V/mm A STM D 149R elative Permittivity, 100 Hz 3.2-A STM D 150R elative Permittivity, 1 MHz 3.2-A STM D 150D issipation Factor, 100 Hz 0.003-A STM D 150D issipation Factor, 1 MHz
0.03-A STM D 150A rc Resistance, Tungsten {PLC}6P LC Code A STM D 495H ot Wire Ignition {PLC)
2P LC Code U L 746A H igh Voltage Arc Track Rate {PLC}3P LC Code U L 746A H igh Ampere Arc Ign, surface {PLC}3P LC Code U L 746A C omparative Tracking Index (UL) {PLC}
2P LC Code U L 746A F LAME CHARACTERISTICS
U L Recognized, 94HB Flame Class Rating (3)0.46m m U L 94U L Recognized, 94V-0  Flame Class Rating (3)0.63m m U L 94U L Recognized, 94-5VA Rating (3)3m m U L 94
O xygen Index (LOI)
30%A STM D 2863U V-light, water exposure/immersion
F 2
-U L 746C
Source, GMD, Last Update:11/09/2009
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS AND PRODUCTS OF THE BUSINESSES MAKING UP THE SABIC INNOVATIVE PLASTICS COMPANY, ITS SUBSIDIARIES AND AFFILIATES ("SABIC IP"), ARE SOLD SUBJECT TO SABIC IP' S STANDARD CONDITIONS OF SALE, WHICH ARE INCLUDED IN THE APPLICABLE DISTRIBUTOR OR OTHER SALES AGREEMENT, PRINTED ON THE BACK OF ORDER ACKNOWLEDGMENTS AND INVOICES, AND AVAILABLE UPON REQUEST.  ALTHOUGH ANY INFORMATION, RECOMMENDATIONS, OR ADVICE
CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SABIC IP MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED,  (I) THAT THE RESULTS DESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (II) AS TO THE EFFECTIVENESS OR SAFETY
OF ANY DESIGN INCORPORATING SABIC IP MATERIALS, PRODUCTS, RECOMMENDATIONS OR ADVICE.  EXCEPT AS PROVIDED IN SABIC IP' S STANDARD CONDITIONS OF SALE, SABIC IP AND ITS REPRESENTATIVES SHALL IN NO EVENT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS OR PRODUCTS DESCRIBED HEREIN.Each ur bears full responsibility for making its own determination as to the suitability of SABIC IP' s materials, products, recommendations, or advice for its own particular u.  Each ur must identify and perform all tests and analys necessary to assure that its finished parts incorporating SABIC IP materials or products will be safe and suitable for u under end-u conditions.  Nothing in this or any other document, nor any oral
recommendation or advice, shall be deemed to alter, vary, superde, or waive any provision of SABIC IP' s Standard Conditions of Sale or this Disclaimer, unless any such modification is specifically agreed to in a writing signed by SABIC IP.  No statement contained herein concerning a possible or suggested u of any material, product or design is intended, or should be construed, to grant any licen under any patent or other intellectual property right of SABIC Innovative Plastics Company or any of its subsidiaries or affiliates covering such u or design, or as a recommendation for the u of such material, product or design in the infringement of any patent or other 1) T ypical  v
alues only. Variations  within  normal tolerances are  possible for vario colours.All values  are measured at least after 48 hours s torage at 230C/50% relative humidity.
All properties, except the melt volume rate are measured on injection m oulded samples.All samples are prepared according to ISO 294.
2) O nly typical data for material lection purpo.Not to be ud for p art or tool design.
3) T his rating is not intended to reflect hazards prented by this or any o ther material under actual fire conditions.4) O wn measurement according to UL.枸橼酸氯米芬
5) Measurements made from laboratory test coupon.  Actual shrinkage may vary outside of range due to
differences in processing conditions, equipment, part geometry and tool design.  It is recommended that mold  shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
V alox* Resin 357
A sia Pacific: COMMERCIAL
P ROCESSING PARAMETERS
TYPICAL VALUE UNIT
I njection Molding
D rying Temperature 120°C D rying Time
3 - 4h rs D rying Time (Cumulative)12h rs M aximum Moisture Content 0.02
%M elt Temperature 250 - 265°C N ozzle Temperature
245 - 260°C F ront - Zone 3 Temperature 250 - 265°C M iddle - Zone 2 Temperature 245 - 260°C R ear - Zone 1 Temperature 240 - 255°C M old Temperature 50 - 75°C B ack Pressure 0.3 - 0.7M Pa S crew Speed
50 - 100r pm S hot to Cylinder Size 40 - 80
%V ent Depth
0.025 - 0.038
周庄在哪
m m
Source, GMD, Last Update:11/09/2009
PLEASE CONTACT YOUR LOCAL SALES OFFICE FOR AVAILABILITY IN YOUR AREA DISCLAIMER : THE MATERIALS AND PRODUCTS OF THE BUSINESSES MAKING UP THE SABIC INNOVATIVE PLASTICS COMPANY, ITS SUBSIDIARIES AND AFFILIATES ("SABIC IP"), ARE SOLD SUBJECT TO SABIC IP' S STANDARD CONDITIONS OF SALE, WHICH ARE INCLUDED IN THE APPLICABLE DISTRIBUTOR OR OTHER SALES AGREEMENT, PRINTED ON THE BACK OF ORDER ACKNOWLEDGMENTS AND INVOICES, AND AVAILABLE UPON REQUEST.  ALTHOUGH ANY INFORMATION, RECOMMENDATIONS, OR ADVICE
CONTAINED HEREIN IS GIVEN IN GOOD FAITH, SABIC IP MAKES NO WARRANTY OR GUARANTEE, EXPRESS OR IMPLIED,  (I) THAT THE RESULTS DESCRIBED HEREIN WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (II) AS TO THE EFFECTIVENESS OR SAFETY
OF ANY DESIGN INCORPORATING SABIC IP MATERIALS, PRODUCTS, RECOMMENDATIONS OR ADVICE.  EXCEPT AS PROVIDED IN SABIC IP' S STANDARD CONDITIONS OF SALE, SABIC IP AND ITS REPRESENTATIVES SHALL IN NO EVENT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS OR PRODUCTS DESCRIBED HEREIN.Each ur bears full responsibility for making its own determination as to the suitability of SABIC IP' s materials, products, recommendations, or advice for its own particular u.  Each ur must identify and perform all tests and analys necessary to assure that its finished parts incorporating SABIC IP materials or products will be safe and suitable for u under end-u conditions.  Nothing in this or any other document, nor any oral
recommendation or advice, shall be deemed to alter, vary, superde, or waive any provision of SABIC IP' s Standard Conditions of Sale or this Disclaimer, unless any such modification is specifically agreed to in a writing signed by SABIC IP.  No statement contained herein concerning a possible or suggested u of any material, product or design is intended, or should be construed, to grant any licen under any patent or other intellectual property right of SABIC Innovative Plastics Company or any of its subsidiaries or affiliates covering such u or design, or as a recommendation for the u of such material, product or design in the infringement of any patent or other 1) T ypical  v
alues only. Variations  within  normal tolerances are  possible for vario colours.All values  are measured at least after 48 hours s torage at 230C/50% relative humidity.
All properties, except the melt volume rate are measured on injection m oulded samples.All samples are prepared according to ISO 294.
2) O nly typical data for material lection purpo.Not to be ud for p art or tool design.
3) T his rating is not intended to reflect hazards prented by this or any o ther material under actual fire conditions.4) O wn measurement according to UL.
5) Measurements made from laboratory test coupon.  Actual shrinkage may vary outside of range due to
differences in processing conditions, equipment, part geometry and tool design.  It is recommended that mold  shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

本文发布于:2023-06-30 07:33:48,感谢您对本站的认可!

本文链接:https://www.wtabcd.cn/fanwen/fan/82/1069775.html

版权声明:本站内容均来自互联网,仅供演示用,请勿用于商业和其他非法用途。如果侵犯了您的权益请与我们联系,我们将在24小时内删除。

标签:波斯   数学   灰指甲   梦见
相关文章
留言与评论(共有 0 条评论)
   
验证码:
推荐文章
排行榜
Copyright ©2019-2022 Comsenz Inc.Powered by © 专利检索| 网站地图