模具和注塑问题点专用英语

更新时间:2023-05-24 16:11:05 阅读: 评论:0

一, weld lines/visible lines/ parting-line:
2. Visible lines here, plea confirm.  此处有熔接线,请确认。
20. Weld lines on visible surface 可见面上有熔接线
21. Parting line proposal/ Parting line description 分型线建议/分型线定义
48. Weld line is obviously on blue region. Advi to cut core inrt to strengthen venting.   蓝色区域有较明显的熔接线,建议做core 侧镶件来加强排气
51. Welding line on the cosmetic surface  熔接线在外表面
二, inrt
3. Sub inrt for air vent  排气镶件
33. Will u the two Holes as a locator with the core inrt (inrt molding)    将用这两个孔去定位Core 侧镶件
54. Venting gap between inrts is too big  镶件处的排气槽过大
91. What the resin for this part? Plea provide detail material brand. 该产品用何材料,请提供具体的材料牌号?
三,texture/surface/painting
8. Surface Texture  表面皮纹
25. Texture (VDI) cavity/ core  cavity/ core的皮纹
26. Special area texture      特殊皮纹区域
34. Will u the two Holes as a locator with the core inrt (inrt molding)    将用这两个孔去定位Core 侧镶件
ick35. Plea confirm texture area and specifications according to the draft figure and texture specification table.    请确认皮纹区域和指定皮纹角度和能力
40. Cosmetic issue  外表面问题
55. Stress mark on the cosmetic surface  产品外表面上有压痕
59. There is black spot on the cosmetic surfacejps  产品外表面上有黑色点人力资源管理的职能
63. There is argent spot  这里有亮点 (银色斑点)
73. Black paint on back side。背面喷黑漆处理。
75. Sharp edge shown in red circle, there may occur as flash or burr issue after painting process, it will impact to paint yield rate. 红色圆圈内的棱角在喷漆后有可能产生飞边现象,增加喷漆返工比率
79. Location hole for spray painting 喷漆工艺孔。obligation
87. Plea confirm this surface is non-cosmetic or not? 请确认该面是否有外观要求?
88. Do there any Cosmetic surface? 是否有任何外观面要求?
95. All the magenta face need to high glossy 所有紫色面需高抛光处理
98. Re-polish the electrode and re-do EDM 电极重新抛光和放电
103 .We have suggested 2 options bad on customer requirement 在客户的基础上我们提供2种方案。
Option 1 will be a better choice we are proposing texture from raw material. 方案1是更好的建议,在粗加工基础上做皮纹处理。
Secondary process is required for option 2 as bending will affect material texture. 方案2,后加工变形会影响产品皮纹。toronto是什么意思
dorian gray
四, remark/mark
9.Remarks on geometry 表面标记
22. Marking of the part  产品标记
23.Comments/ open issues    问题点
77. Core side no any marks  后模无任何标记
五, wall thickness
10. Analysis wall thickness  产品壁厚分析
11. Thick ction, propo to reduce plastic to keep even wall. 产品厚壁部份,建议减胶以保持均匀壁厚
56. Uneven thickness  不平均的产品壁厚
69. It is too thin and very difficult to inject fully, and weakness wall will have risk of the part function  该处壁厚过薄而造成很难去填充完整,薄壁将会有产品功能上的风险。
70. The are will have sink marks due to uneven thickness, propo to reduce plastic. 壁厚不均匀容易产生缩印,建议在该处减胶。
72 . Plea confirm the 3D part thickness whether has including painting thickness or not? 请确认产品的设计是否考虑到油漆的厚度.
74. Average wall thickness is 0.50 only, Max is 0.74. It is too thin and very difficult to inject
fully. 产品均厚仅有0.5mm免费学英语软件,最厚为0.74mm, 产品整体壁厚太薄,很难成型饱满。
81. This part is a thin wall product, the average wall thickness is only 0.5. We suggest using high speed machine to mold such thin product. Numbers of venting inrt on core is necessary to exhaust the air from inside to outside. 该薄壁件壁厚仅为0.5mm,建议使用高压注塑机成型。 在后模侧的一定数量的排气镶件利于成型。
83.ropo to reduce plastic form 1.02mm to 0.9mm as right picture shown to avoid sticking cavity side. 右图示的区域建议减胶从1.2mm到0.9mm,以避免前模粘模。
nasa是什么六, sink marks
50. High shrinkage values could indicate sink marks or voids at gate location  高缩水率的产品容易产生缩印,但在浇口附近可以避免
61. for one more daythere is sink mark on the cosmetic surface  产品外表面上有缩痕
71. The are will have sink marks due to ribs opposite.  正面的筋位易导致背面产生缩印。
104. Sink mark will occur on yellow region. Becau of thickness vibration, it is no u to increa gate size. 由于壁厚的震动导致黄色区域会有缩印,没有必要增加浇口尺寸。
106 . Plea keep intend on sink mark problem 请关注缩印问题。
110. The gust is too thick to lead to sink mark on the opposite surface.    圆筒壁太厚引起反面缩印。
118. Higher the package, smaller the sink mark. 背压提升会减小缩印。
七, thin steel/ thin wall
12. Weak steel 薄铁
84. Propo to remove the red radius to avoid thin steel. 为避免尖铁建议去除红色的圆角
八, flash
60. There is flash on the product  产品有飞边
53. Venting inrt here has flash  排气镶件处有飞边
九, draft
13.Draft analysis Cavity/Core  广州心理咨询师培训Cavity/Core的脱模角分析
14.All the green face no draft, propo to add 1degree on core side/cavity side for part relea.                          所有的绿色面没有脱模角,建议加1°在core侧/ cavity侧为产品出模。
15.All the green face 1.0 degree on cavity side, propo to rever to 1.0 degree on core side to avoid sticking cavity side.                                     
    所有的绿色面1°脱模角在cavity侧,建议加做反1°在core侧防止产品粘前模。

本文发布于:2023-05-24 16:11:05,感谢您对本站的认可!

本文链接:https://www.wtabcd.cn/fanwen/fan/78/760156.html

版权声明:本站内容均来自互联网,仅供演示用,请勿用于商业和其他非法用途。如果侵犯了您的权益请与我们联系,我们将在24小时内删除。

标签:产品   建议   缩印   皮纹   区域   产生   排气   增加
相关文章
留言与评论(共有 0 条评论)
   
验证码:
推荐文章
排行榜
Copyright ©2019-2022 Comsenz Inc.Powered by © 专利检索| 网站地图